Abstract:In this article, we report a novel, nanoprecipitation-based method for preparing silica nanoparticles with thiol and amine cofunctionalization. (3-Mercaptopropyl)trimethoxysilane (MPTMS) and 3-aminopropyltrimethoxysilane (APTMS) were used as the organosilane precursors, which were subjected to acid-catalyzed polycondensation in an organic phase containing a water-miscible solvent (e.g., dimethyl sulfoxide). A pale colloidal solution could be immediately formed when the preincubated organic phase was directly injected into water. The initial composition ratio between MPTMS and APTMS is an important factor governing the formation of nanoparticles. Specifically, large, unstable micrometer-sized particles were formed for preparation using MPTMS as the sole silane source. In contrast, when APTMS was used alone, no particles could be formed. By reducing the fraction of APTMS (or increasing that of MPTMS) in the initial mixture of organosilanes, the formation of nanometer-sized particles occurred at a critical fraction of APTMS (i.e., 25%). Remarkably, a tiny fraction (e.g., 1%) of APTMS was sufficient to produce stable nanoparticles with a hydrodynamic diameter of about 200 nm. Other factors that would also affect particle formation were determined. Moreover, an interesting temperature effect on particle formation was observed. The TEM micrographs show spherical nanospheres with mean sizes of 130-150 nm in diameter. The solid-state (29)Si NMR spectra demonstrate that the hybrid silica materials contain fully and partially condensed silicon structures. The bifunctionalized silica nanoparticles have positive zeta potentials whose magnitudes are positively correlated with the amount of APTMS. The total thiol content, however, is negatively correlated with the amount of APTMS. The cationic nanoparticles can bind an antisense oligonucleotide in a composition-dependent manner.

Synthesis of Anisotropic Silica Nanoparticles

Synthesis of Amino Group Functionalized Monodispersed Mesoporous Silica Nanospheres Using Anionic Surfactant

Synthesis Of Nonspherical Mesoporous Silica Ellipsoids With Tunable Aspect Ratios For Magnetic Assisted Assembly And Gene Delivery

Recent Advances in the Synthesis and Applications of Anisotropic Carbon and Silica-Based Nanoparticles

Anionic Surfactants Templating Route for Synthesizing Silica Hollow Spheres with Different Shell Porosity

Controllable Synthesis of Anisotropic Silica/polymer Composite Particles Via Seeded Dispersion Polymerization

Synthesis of Patchy Nanoparticles with Symmetry Resembling Polar Small Molecules

Synthesis and Formation Mechanism of Aminated Mesoporous Silica Nanoparticles

Facile Synthesis of Size Controllable Dendritic Mesoporous Silica Nanoparticles

Single Copolymer Chain‐Templated Synthesis of Ultrasmall Symmetric and Asymmetric Silica‐Based Nanoparticles

Synthesis of Anisotropic Polymer/Inorganic Particles Via Asymmetric Swelling-Dissolving Process

A novel approach to the synthesis of hollow silica nanoparticles

Synthesis of silica nanoparticles from sodium silicate under alkaline conditions

Versatile Synthesis of Thiol- and Amine-Bifunctionalized Silica Nanoparticles Based on the Ouzo Effect

Preparation of Highly Monodisperse Hybrid Silica Nanospheres Using a One-Step Emulsion Reaction in Aqueous Solution

Emulsion-Guided Controllable Construction of Anisotropic Particles: Droplet Size Determines Particle Structure

Synthesis of Chemically Asymmetric Silica Nanobottles and Their Application for Cargo Loading and as Nanoreactors and Nanomotors

Well-Defined Homopolymer Nanoparticles with Uniaxial Molecular Orientation by Synchronized Polymerization and Self-Assembly

Ultrasonic Synthesis of Silica−Alumina Nanomaterials with Controlled Mesopore Distribution Without Using Surfactants

A general method to synthesize a family of mesoporous silica nanoparticles less than 100 nm and their applications in anti-reflective/fogging coating

Synthesis, Surface Modification and Biological Imaging of Aggregation-Induced Emission (AIE) Dye Doped Silica Nanoparticles