Abstract:Photothermal catalytic oxidation is a promising and sustainable method for the degradation of indoor formaldehyde (HCHO). However, the excessively high surface temperature of existing photothermal catalysts during catalysis hinders the effective adsorption and degradation of formaldehyde under static conditions. Catalyst loading and oxygen vacancies (OVs) modulation are commonly employed strategies to reduce the photothermal catalytic temperature and enhance the efficiency of photothermal catalytic oxidation. In this work, a p-n type CuO/TiO2 heterojunction is successfully loaded onto diatomite using a wet precipitation method. Under the irradiation of a 300W xenon lamp, the prepared composite material achieved a 100% removal rate of HCHO within 2 h, with a 98% conversion rate to CO2, surpassing the performance of both individual photocatalysts and thermocatalysts. Additionally, by adjusting conditions such as light irradiation and temperature, we have demonstrated that this material exhibits synergistic photothermal catalytic properties. Based on HRTEM, XPS, Raman, and EPR analyses, the introduction of diatomite as a catalyst support was shown to effectively increase the number of OVs. Experimental results, along with O2-TPD, photoelectrochemical characterization, and radical detection, demonstrate that the presence of OVs enhances the oxidative efficiency of both photocatalysis and thermocatalysis, as well as the UV-Vis-IR photothermal catalytic performance. The ternary composite material generates weak hydroxyl (•OH) and superoxide (•O2-) radical under high-temperature with dark conditions, indicating its catalytic oxidation activity under this condition. The increase in temperature and the expansion of the spectral range both enhance the generation of these radicals. In summary, this work demonstrates that the use of diatomite as a support increases the material's specific surface area and OVs content, thereby enhancing adsorption and photothermal catalysis. It elucidates the enhanced catalytic degradation mechanism of this mineral-based photothermal catalyst.

In Situ Synthesis of Mesoporous TiO2 Doped with Bismuth Single Atoms for Tunable Photocatalytic Degradation of Formaldehyde

Development of Titanium Oxide-Based Mesoporous Materials in Photocatalysis

Synthesis of Nano-Tio2/diatomite Composite and Its Photocatalytic Degradation of Gaseous Formaldehyde

One-Step Synthesis Of Bifunctional Tio2 Catalysts And Their Photocatalytic Activity

The Application of Bi‐Doped TiO 2 for the Photocatalytic Oxidation of Formaldehyde

Single Mn atom modulated molecular oxygen activation over TiO2 for photocatalytic formaldehyde oxidation

The intrinsic effects of oxygen vacancy and doped non-noble metal in TiO2(B) on photocatalytic oxidation VOCs by visible light driving

Controllable Synthesis and Tunable Photocatalytic Properties of Ti3+-doped TiO2

In Situ Synthesis of the Mesoporous C–TiO2 Microspheres Derived from Partial Hydrolysis Tetrabutyl Titanate for Enhanced Photocatalytic Degradation under Visible Light

Bismuth-doped ordered mesoporous TiO2: visible-light catalyst for simultaneous degradation of phenol and chromium.

Single-Atom Fe Triggers Superb CO 2 Photoreduction on a Bismuth-Rich Catalyst

Metal–organic frameworks derived C/TiO2 for visible light photocatalysis: Simple synthesis and contribution of carbon species

Directed Synthesis of Mesoporous TiO2 Microspheres: Catalysts and Their Photocatalysis for Bisphenol A Degradation.

Generation of oxygen vacancies in CuO/TiO2 heterojunction induced by diatomite for highly efficient UV-Vis-IR driven photothermal catalytic oxidation of HCHO

Selective activation of dioxygen to singlet oxygen over La-Si co-doped TiO2 microspheres for photocatalytic degradation of formaldehyde

Solar Light Photocatalysis Using Bi2O3/Bi2SiO5 Nanoheterostructures Formed in Mesoporous SiO2 Microspheres

Micellar Interface Modulation Self-Assembly Strategy Towards Mesoporous Bismuth Oxychloride-Based Materials for Boosting Photocatalytic Pharmaceuticals Degradation

Self-assembly of BixTi1−xO2 Visible Photocatalyst with Core–shell Structure and Enhanced Activity

Self-Assembly of Active Bi2O3/TiO2 Visible Photocatalyst with Ordered Mesoporous Structure and Highly Crystallized Anatase

Facile hydrothermal synthesis of TiO2-Bi2WO6 hollow superstructures with excellent photocatalysis and recycle properties.

Facile Fabrication of Mesoporous SiO2@(cTiO2/BiOI) Heterojunctions with Enhanced Photocatalytic Properties Due to Large Surface Area for Contact with Pollutants