Highly active bimetallic MOF derivatives for improving the dehydrogenation performance of LiAlH 4
Yiting Bu,Lixian Sun,Fen Xu,Sheng Wei,Federico Rosei,Yumei Luo,Zhaoyu Liu,Jiaxi Liu,Chenchen Zhang,Yuan Yao
DOI: https://doi.org/10.1016/j.jallcom.2023.170897
IF: 6.2
2023-06-28
Journal of Alloys and Compounds
Abstract:LiAlH 4 is considered an effective hydrogen storage material due to its high hydrogen storage capacity and relative abundance of aluminum. However, LiAlH 4 presents disadvantages such as slow kinetics, high dehydrogenation temperature, and poor reversibility. To improve these shortcomings of LiAlH 4 , we designed and prepared Ni-Ti bimetallic metal-organic framework derivatives with stable structures and high dispersion of metal species, which named as Ni-Ti-NC. A series of tests show that the composite components and circular disk-like structure of Ni-Ti-NC can improve the dehydrogenation behavior of LiAlH 4 . Benefiting from the addition of Ni-Ti-NC, the initial decomposition temperature of LiAlH 4 significantly decreased to 59.5 °C, and about 6.11 wt% of hydrogen was rapidly released within 25 min at 200 °C. Meanwhile, the activation energies of the two-step hydrogen evolution reaction decreased to 64.18 kJ·mol −1 and 73.99 kJ·mol −1 , respectively. Furthermore, compared with only 0.09 wt% hydrogen absorption of pure LiAlH 4 at 30 bar hydrogen pressure and 300 °C constant temperature, doping Ni-Ti-NC promoted the hydrogen absorption capacity of LiAlH 4 to nearly 0.64 wt% under the same conditions. In addition, the structure and chemical changes of LiAlH 4 after the addition of Ni-Ti-NC were investigated in detail. The reasons why Ni-Ti-NC improved the hydrogen storage performance of LiAlH 4 were comprehensively analyzed, which helped us design efficient catalysts for solid hydrogen storage materials.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering