Abstract:The corrosion resistance of titanium alloy poses a crucial challenge, significantly affecting its prospect for service and application. The present study aimed to investigate the corrosion resistance of Ti-6Al-4V ELI alloys with varying surface roughness in hydrofluoric acid solution, in order to assess the influence of roughness on their corrosion resistance performance. The weight loss percentage, surface morphology evolution, and roughness variation of Ti-6Al-4V ELI alloys before and after exposure to hydrofluoric acid corrosion were characterized. While the weight loss and weight loss percentage of the Ti-6Al-4V ELI alloy increased with prolonged corrosion, the overall weight loss rate decreased. The accumulation of TiF3 phases and depletion of the Ti-6Al-4V ELI matrix mutually led to the alterations of the surface roughness. Due to the inability to prevent fluoride ions from contacting with the Ti-6Al-4V ELI alloy, continuous corrosion occurred in hydrofluoric acid. Based on these experimental results and analysis, the corrosion mechanism of the Ti-6Al-4V ELI alloy corroded by hydrofluoric acid solution was elucidated. Furthermore, an analysis was conducted to explore the influence of corrosion time on mechanical properties by analyzing the decay in compressive properties of the Ti-6Al-4V ELI titanium alloy after hydrofluoric acid corrosion treatment. The bearing capacity of the Ti-6Al-4V ELI alloy deteriorated over the corrosion time.

Nanoscale Pitting Corrosion of Commercially Pure Ti in Solution Containing Fluoride Ion

The Effect on the Corrosion Resistance of Ti Alloy in the Artificial Saliva with Different pH Value

Corrosion behaviour of a wrought Ti-6Al-3Nb-2Zr-1Mo alloy in artificial seawater with various fluoride concentrations and pH values

Effect of Ph Value and Fluoride Ions on Corrosion Resistance of Pure Ti and Ni-Cr-Ti Alloy in Artificial Saliva

Comparison of the corrosion behavior of pure titanium and its alloys in fluoride-containing sulfuric acid

Corrosion Behavior of TiNi Alloy Fabricated by Selective Laser Melting in Simulated Saliva

Understanding the effect of fluoride on corrosion behavior of pure titanium in different acids

Nanoscale corrosion investigation of surface nanocrystallized 7150 Al alloy in 3.5 wt% NaCl solution by using FIB-TEM techniques

Hydrothermal oxidation of titanium nitride coating for enhanced corrosion resistance in fluoride-containing acidic solution

Elucidating the effect of titanium alloying on the pitting corrosion of ferritic stainless steel

INFLUENCE OF FLUORIDE ION CONCENTRATIONS ON THE CORROSION BEHAVIOR OF Ta2N NANOCRYSTALLINE COATING FOR DENTAL IMPLANT APPLICATIONS

Understanding the Pitting Mechanism of Super Ferritic Stainless Steel in Bromide Solutions: the Role of Ti/Nb–Mo Precipitates with a Core–shell Structure

(Digital Presentation) Corrosion-Resistance Investigation of Titanium Passive Layer in Acidic Solution

The corrosion behavior of Ti6Al4V fabricated by selective laser melting in the artificial saliva with different fluoride concentrations and pH values

Effects of cavitation erosion-induced surface damage on the corrosion behaviour of TA31 Ti alloy

Metastable pitting corrosion behavior of laser powder bed fusion produced Ti-6Al-4V in Hank’s solution

(Digital Presentation) Anti-Corrosion Investigation of Titanium Electrode for Cu Plating

Corrosion Behavior in Hydrochloric Acid of Pure Titanium after Ultrasonic Severe Surface Rolling

Microstructure evolution and corrosion mechanism of in situ synthesized TiC/TC4 alloy nanocomposites fabricated by laser powder bed fusion

Salt spray corrosion behavior and pitting resistance of Ti-15 V-3Cr-3Al-3Sn alloy evaluated using XPS, SKPFM, and electrochemical technique

The Study on Corrosion Resistance of Ti-6Al-4V ELI Alloy with Varying Surface Roughness in Hydrofluoric Acid Solution