Ultrahigh Energy Storage Density and Efficiency in Bi 0.5 Na 0.5 TiO 3 -Based Ceramics via the Domain and Bandgap Engineering
Meng Wang,Qin Feng,Chaoying Luo,Yuchen lan,Changlai Yuan,Nengneng Luo,Changrong Zhou,Toyohisa Fujita,Jiwen Xu,Guohua Chen,Yuezhou Wei
DOI: https://doi.org/10.1021/acsami.1c14151
2021-10-21
Abstract:Environmentally friendly lead-free dielectric ceramics have attracted wide attention because of their outstanding power density, rapid charge/dischargerate, and superior stability. Nevertheless, as a hot material in dielectric ceramic capacitors, the energy storage performance of Na<sub>0.5</sub>Bi<sub>0.5</sub>TiO<sub>3</sub>-based ceramics has been not satisfactory because of their higher remnant polarization value and low dielectric breakdown strength, which is a problem that must be urgently overcome. In this work, the (1 - <i>x</i>) (0.6Na<sub>0.5</sub>Bi<sub>0.5</sub>TiO<sub>3</sub> - 0.4Sr<sub>0.7</sub>Bi<sub>0.2</sub>TiO<sub>3</sub>) - <i>x</i>Ba(Mg<sub>1/3</sub>Ta<sub>2/3</sub>)O<sub>3</sub> (BNST-<i>x</i>BMT) systems were designed based on a dual optimization strategy of domain and bandgap to solve the above problems. As a result, a record-breaking ultrahigh energy density and excellent efficiency (<i>W</i><sub>rec</sub> = 8.58 J/cm<sup>3</sup>, η = 93.5%) were obtained simultaneously under 565 kV/cm for the BNST-0.08BMT ceramic. The introduction of Sr<sub>0.7</sub>Bi<sub>0.2</sub>TiO<sub>3</sub> induces the formation of nanodomains in BNT-based ceramics, leading to slim <i>P</i>-<i>E</i> curves, and the further modification of Mg/Ta reduces the grain sizes and increases the bandgap width, resulting in significant enhancement of the dielectric breakdown strength. Moreover, excellent stability and superior discharge performance (<i>W</i><sub>d</sub> = 4.7 J/cm<sup>3</sup>, <i>E</i> = 320 kV/cm) in the BNST-0.08BMT ceramic were also achieved. The results suggest that the BNST-0.08BMT ceramic shows potential applicability for dielectric energy storage ceramics. Simultaneously, the composition-design concept in the system provides a good reference for the further development of ceramic dielectric capacitors.
materials science, multidisciplinary,nanoscience & nanotechnology