Abstract:Uniform and well-dispersed SiO2:x%Tb3+@Lu2O3:y%Eu3+ core-shell spherical phosphors were synthesized via a solvothermal method followed by a subsequent calcination process. The structure, phase composition, and morphology of the samples were studied by X-ray diffraction (XRD), thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FT-IR), field emission scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The results showed that the Lu2O3 :Eu3+ layer was evenly coated on the surface of SiO2:Tb3+ spheres and the shell thickness was about 45-65 nm. The PL spectra and fluorescence lifetimes of the samples were further studied. It was proved that the multicolor luminescence of the samples could be realized by changing the doping concentration ratio of Eu3+ or by changing the excitation wavelengths. Compared with SiO2@Lu2O3:3%Tb3+,6% Eu3+, SiO2:3%Tb3+@Lu2O3 :6%Eu3+ showed stronger luminescence intensity, longer fluorescence lifetime, and higher energy transfer efficiency, which was attributed to the effective interfacial energy transfer, and the interfacial energy transfer mechanism from Tb3+ to Eu3+ was a dipole-dipole interaction mechanism. The XPS results indicated that the sample contained a high content of Si-O-Lu bonds, which proved that there was a strong interaction between the SiO2 core and the Lu2O3 shell, making the interfacial energy transfer possible. These results provided a new idea for luminescence enhancement and multicolor luminescence.

A Comparative Study of SiO2:Tb3+@Gd2O3:Eu3+ and Its Inverted Tb3+-Eu3+ Core-Shell Phosphors

A Comparative Study of SiO2:Tb3+@Gd2O3:Eu3+ and Its Inverted Tb3+-Eu3+ Core-Shell Phosphors.

A Comparative Study of SiO 2 :Tb 3+ @Gd 2 O 3 :Eu 3+ and Its Inverted Tb 3+ -Eu 3+ Core-Shell Phosphors

SiO<sub>2</sub>:Tb<SUP>3+</SUP>@Lu<sub>2</sub>O<sub>3</sub>:Eu<SUP>3+</S UP>Core-Shell Phosphors: Interfacial Energy Transfer for Enhanced Multicolor Luminescence

Photoluminescent Properties of Eu3+ and Tb3+ Codoped Gd2O3 Nanowires and Bulk Materials

Controlled Synthesis of Tb3+/Eu3+ Co-Doped Gd2O3 Phosphors with Enhanced Red Emission

Controlled Synthesis of Tb/Eu Co-Doped Gd₂O₃ Phosphors with Enhanced Red Emission.

Tunable Multicolor Emission and Energy Transfer of Cylindrical Gd2O3:Dy3+, Tb3+, Eu3+ Particles

Controlled Synthesis of Tb<sup>3+</sup>/Eu<sup>3+</sup> Co-Doped Gd<sub>2</sub>O<sub>3</sub> Phosphors with Enhanced Red Emission

Luminescence Properties and Ce3+→Tb3+ Energy Transfer of Li2SrSiO4:Ce3+ ,Tb3+ Phosphor

Enhanced luminescence efficiency and thermal stability via introduction of non-rare earth Bi3+ in Gd5Si2BO13:Eu3+

Novel Color-Tunable Gd2o2cn2:Tb3+, Eu3+ Phosphors: Characterization and Photoluminescence Properties

Photoluminescence Tuning Via Energy Transfer in Eu-Doped Ba-2(Gd,Tb)(2)Si4o13 Solid-Solution Phosphors

Luminescence Intensity Enhancement of Eu2+and Eu3+by Tb3+in LiLa9(SiO4)6O2

Multi-color Luminescence and Energy Transfer Behavior of Ba3Lu4O9:Tb3+,Eu3+ Phosphor for Solid-State Lighting

Luminescence Properties and Energy Transfer of Sr3 Gd0.5 -Xtb0.5 ( BO3 ) 3∶ Xeu3 +

Luminescence and Energy Transfer of A Color Tunable Phosphor: Tb3+ and Eu3+ Co-Doped Scpo4

Photoluminescence Tuning Via Energy Transfer in Eu-doped Ba2(Gd,Tb)2Si4O13 Solid-Solution Phosphors

Luminescent properties and energy transfer mechanism from Tb3+ to Eu3+ in color adjustable nano Ca5(PO4)3(OH): Eu3+,Tb3+ phosphors

Luminescence Properties and Energy Transfer of Tb3+, Eu3+ Co-Doped YTaO4 Phosphors Obtained Via Sol–gel Combustion Process

Energy Transfer and Multicolor Tunable Emission in Single-Phase Tb3+, Eu3+ Co-Doped Sr3La(PO4)3 Phosphors