Abstract:Sodium vanadium oxyfluorophosphate Na 3 V 2 (PO 4 ) 2 F 2 O is an attractive cathode material for sodium ion batteries due to its high crystalline stability, high specific capacity and high discharge potential. Currently, the poor electronic conductivity and low diffusion rate of Na + severely impede its development and application. In this work, low-dose Mo 2+ doping is proposed through first-principle computation to enhance the structure and performance of Na 3 V 2 (PO 4 ) 2 F 2 O. It is found that low-dose of Mo 2+ doping can reduce the band gap and energy barrier for Na + diffusion in Na 3 V 2 (PO 4 ) 2 F 2 O. However, heavy doping leads to serious Jahn-Teller distortion of the crystal structure. Therefore, low-dose Mo 2+ doping, ranging from x = 0 to x = 0.06 in Na 3 V 2-x Mo x (PO 4 ) 2 F 2 O, is designed and experimentally carried out. The best performance with 118.5 mA h g -1 at 0.1C and 60.6 mA h g -1 at 20C is obtained in Na 3 V 1.96 Mo 0.04 (PO 4 ) 2 F 2 O when x = 0.04 in comparison with other doping amounts. The specific discharge capacity at 0.5C decreases gradually from 105.4 to 77.9 mA h g -1 after 400 cycles, indicating a capacity retention of 73.9 %. These results demonstrate that low-dose Mo 2+ doping is an effective strategy to enhance the electrochemical performance of Na 3 V 2 (PO 4 ) 2 F 2 O, making it a promising cathode material for sodium batteries.

Mechanism and Enhanced Performance of Low-Dose Low-Valence Molybdenum-Doped Na 3 V 2 (PO 4 ) 2 F 2 O Cathodes for Sodium Batteries