Fabrication of Titanium Aluminide Alloys by Twin-Wire Tungsten Inert Gas Welding Applied with High-Frequency Induction Heating Wire Technology: Processing, Microstructure, and Properties
Ze Li,Zhiyong Li,Jieliang Ren,Haiwu Zhou,Yingqiao Zhang,Shouzheng Wei,Yichuan Zhang,Fuqiang Liu
DOI: https://doi.org/10.1007/s11665-024-09329-2
IF: 2.3
2024-03-27
Journal of Materials Engineering and Performance
Abstract:Titanium aluminide (TiAl) alloys are promising high-temperature structural materials in the aerospace field. The wire-arc directed energy deposition (WA-DED) is a desirable process for fabricating TiAl alloys. However, it is hard to ensure Ti wire and Al wire melt simultaneously under the heat of one single arc, so the TiAl alloys with homogeneous composition and uniform microstructure are hard to obtain. Therefore, this paper proposes an innovative twin-wire TIG welding process applied with high-frequency induction heating wire technology. The wire feeding speed of the two wires was adjusted separately to fabricate Ti-50Al alloy weld metal. When the Ti wire was preheated to 350 °C (hot wire (350 °C)), both wires melted simultaneously and the droplets were evenly transferred to the weld pool. The hot-wire (350 °C) specimen has an Al content of approximately 50 at.% in different regions. Its microstructures are duplex phase, consisting of α 2 /γ lamellae with γ phases distributed at the grain boundaries. When the Ti wire was fed at room temperature (cold wire), the deflection of the droplet toward the side of the Al wire prevented both wires from melting and entering the weld pool simultaneously, ultimately resulting in uneven metal transfer. In the cold-wire specimen, the Al content varies greatly in different regions, showing different microstructural characteristics. The hardness, wear rate, corrosion potential, and corrosion current also show substantial variation across different regions of the cold-wire specimen. In contrast, differences in the hot-wire (350 °C) specimen are comparatively minor. The results show that the hot-wire process has the potential to fabricate TiAl alloys with homogeneous composition, uniform microstructure, and stable properties.
materials science, multidisciplinary