Abstract:The inevitable agglomeration of metal nanoparticles during catalysis is a lethal factor leading to catalyst deac-tivation. Functional fiber-based catalysts may be a solution to this problem. This study describes a novel func-tionalized fiber with a bis (N -heterocyclic carbene) (bis(NHC)) structure, which was constructed using polyacrylonitrile fiber (PANF). Palladium nanoparticles were loaded onto the proposed fiber, demonstrating that they provided both particle size control and an excellent anti-agglomeration effect. The fiber samples were fully characterized using Fourier transform infrared spectroscopy (FTIR), X-ray diffraction tests (XRD), and X-ray photoelectron spectroscopy (XPS). The particle sizes of Pd nanoparticles and physical properties of the fiber samples were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), thermogravimetric analysis (TGA), energy dispersive spectrometer (EDS), and mechanical property analysis. The proposed functional fiber was applied to effectively catalyze the Heck reaction with high catalytic activity (20 min-60 min) and a wide range of substrate applications (19 examples). Besides, it can be recycled twenty times without deactivation. TEM results proved that PANbis(NHC)F effectively inhibits particle agglomeration (4-10 nm after 20 cycles) during the catalytic process, thereby maintain the high activity of the catalyst. In addition, highly polar reactants were found to be beneficial to the improvement of the reactivity during the substrate expansion process, and a possible fiber-based polar microenvironment mechanism was proposed based on the results.

Easily Recyclable Pd-Decorated Hierarchically Porous Nanofibers for the Selective Hydrogenation of Phenol

Pd-Decorated Hierarchically Porous Carbon Nanofibers for Enhanced Selective Hydrogenation of Phenol

Pd Nanoparticles Supported on Hierarchically Porous Carbon Nanofibers As Efficient Catalysts for Phenol Hydrogenation

Pd Nanoparticles Decorated ZIFs/polymer Core-Shell Nanofibers Derived Hierarchically Porous N-doped Carbon for Efficient Catalytic Conversion of Phenol

Synergistic Effects of Hierarchically Porous Structures and Amino Groups in Pd@MOFs for the Selective Hydrogenation of Phenol

Controllable Synthesis of 1D Pd@N-CNFs with High Catalytic Performance for Phenol Hydrogenation

Well-Defined MOF-Derived Hierarchically Porous N-Doped Carbon Materials for the Selective Hydrogenation of Phenol to Cyclohexanone

Knitting N-doped Hierarchical Porous Polymers to Stabilize Ultra-small Pd Nanoparticles for Solvent Free Catalysis.

Hierarchical Pd@PC-COFs As Efficient Catalysts for Phenol Hydrogenation

Pd Nanoparticles Loaded on Two-Dimensional Covalent Organic Frameworks with Enhanced Catalytic Performance for Phenol Hydrogenation

Ultrafine Palladium Nanoparticles Deposited on Ni, N Co-Doped Carbon to Boost Dehydrogenation Efficiency of Perhydro-N-Phenylcarbazole

Fabrication of Pd@N-doped Porous Carbon-Tio2 As a Highly Efficient Catalyst for the Selective Hydrogenation of Phenol to Cyclohexanone in Water

Preparation and Application of the Bifunctional Pd/ZrHP Catalyst for Selective Hydrogenation of Phenol

Hierarchical Pd@ZIFs As Efficient Catalysts for P-Nitrophenol Reduction

Dendrimer-Encapsulated Pd Nanoparticles, Immobilized in Silica Pores, as Catalysts for Selective Hydrogenation of Unsaturated Compounds

Space-Confined Carbon-Doped Pd Nanoparticles as a Highly Efficient Catalyst for Selective Phenol Hydrogenation

Controllable Synthesis of Micro-Mesoporous Pd@N-doped Carbon Derived from ZIF@NiCoLDH for Enhanced Phenol Hydrogenation to Cyclohexanone

Smart Design Of Small Pd Nanoparticles Confined In Hollow Carbon Nanospheres With Large Center-Radial Mesopores

Regulating the electronic state of Pd nanoclusters and Lewis acid density by the carbon doping for synergistically enhancing phenol hydrogenation in green solvent

Flexible Hierarchical Pd/SiO2-TiO2 Nanofibrous Catalytic Membrane for Complete and Continuous Reduction of P-Nitrophenol

Functional Fiber with Bis (N-Heterocyclic Carbene) Structure Prevents Pd(0) Nanoparticle Agglomeration for an Efficient and Recyclable Heck Reaction