Impact of Ultrafast Demagnetization Process on Magnetization Reversal in L1 FePt Revealed Using Double Laser Pulse Excitation
J. Y. Shi,M. Tang,Z. Zhang,L. Ma,L. Sun,C. Zhou,X. F. Hu,Z. Zheng,L. Q. Shen,S. M. Zhou,Y. Z. Wu,L. Y. Chen,H. B. Zhao
DOI: https://doi.org/10.1063/1.5017148
IF: 4
2018-01-01
Applied Physics Letters
Abstract:Ultrafast laser induced magnetization reversal in L10 FePt films with high perpendicular magnetic anisotropy was investigated using single- and double-pulse excitations. Single-pulse excitation beyond 10 mJ cm−2 caused magnetization (M) reversal at the applied fields much smaller than the static coercivity of the films. For double-pulse excitation, both coercivity reduction and reversal percentage showed a rapid and large decrease with the increasing time interval (Δt) of the two pulses in the range of 0–2 ps. In this Δt range, the maximum demagnetization (ΔMp) was also strongly attenuated, whereas the integrated demagnetization signals over more than 10 ps, corresponding to the average lattice heat effect, showed little change. These results indicate that laser induced M reversal in FePt films critically relies on ΔMp. Because ΔMp is determined by spin temperature, which is higher than lattice temperature, utilizing an ultrafast laser instead of a continuous-wave laser in laser-assisted M reversal may reduce the overall deposited energy and increase the speed of recording. The effective control of M reversal by slightly tuning the time delay of two laser pulses may also be useful for ultrafast spin manipulation.