Abstract:Detailed NMR investigations on fresh and coked Mo/HMCM-22 catalysts for methane dehydro-aromatization were presented. Al-27 MAS and Si-29 MAS as well as corresponding CP/MAS NMR experiments have proved that an interaction between molybdenum and the zeolite lattice occurs during the impregnation and calcination processes of the catalysts. With Bronsted acid sites serving as a powerful trap, molybdenum migrates into the internal channels of the zeolite and reacts preferentially with bridging hydroxyls groups. Thus, molybdenum is anchored to the framework aluminum through an oxygen bridge, which, in turn, modifies the acidic properties of the HMCM-22 and leads to a high dispersion of the molybdenum. If this kind of interaction becomes stronger, expelling of aluminum from the zeolite lattice would occur, with the forming of both octahedral nonframework aluminum and Al-2(MoO4)(3) crystallites, The latter can be hydrated to [Al(OH)(n)(H2O)(6-n)](n)(MoO4) (n = 1 or 2) in a water-saturated desiccator and can give a line at ca. 14 ppm in the Al-27 MAS NMR spectrum. UV-Raman results suggest that the carbonaceous deposits on the catalysts are mainly hydrogen-deficient aromatic type, which are also verified by H-1 --> Si-29 CP/MAS and H-1 --> Al-27 CP/MAS NMR, as well as the failure for conducting the C-13 CP/MAS NMR experiment. H-1 --> Al-27 CP/MAS NMR experiments indicate that most of the coke is deposited on framework aluminum (Bronsted site). Regeneration in an oxygen atmosphere leads to the formation of a considerable amount of Al-2(MoO4)(3) crystallites. However, the catalytic activity can be properly restored after the regeneration; thus, the idea of taking this species as the detrimental factor for this reaction can be ruled out. On the other hand, lattice destruction of the zeolite is suggested to be responsible for the poor performance exhibited by the 10Mo/HMCM-22 catalyst. The synergic effect between molybdenum and Bronsted acid sites is considered to be the main reason for the outstanding catalytic performance of the 6Mo/HMCM-22 catalyst.

Fabrication and Catalytic Tests of MCM-22/silicon Carbide Structured Catalysts.

Template‐Synthesized Porous Silicon Carbide As an Effective Host for Zeolite Catalysts

Synthesis and Catalytic Performance of MCM-22 Molecular Sieves with High Molar Ratio of SiO_2 to Al_2O_3

Structured zeolites catalysts with hierarchical channel structure.

Synthesis of mesoporous molecular sieves and their application as supports for catalysts in F-T synthesis

Direct Ink Writing of Hierarchical Porous SiC Ceramics As Catalyst Support for Hydrogen Production

Si/Al Ratio Induced Structure Evolution During Desilication-Recrystallization of Silicalite-1 to Synthesize Nano-Zsm-5 Catalyst for MTH Reaction

A hybrid sol–gel synthesis of mesostructured SiC with tunable porosity and its application as a support for propane oxidative dehydrogenation.

Preparation and Catalytic Performance of Noble Metal Loaded Core-Shell Structured Catalyst

Methane Dehydroaromatization on Mo/Hmcm-22 Catalysts: Effect of Sio2/Al2o3 Ratio of Hmcm-22 Zeolite Supports

Sustainable Synthesis of Core-shell Structured ZSM-5@Silicalite-1 Zeolite

Catalytic Activities and Properties of Sulfated Zirconia Supported on Mesostructured Γ-Al2o3

Al Distribution of MWW Zeolites and Its Correlation with Catalytic Performance in Direct Syngas Conversion

Coating mesoporous ZSM-5 by microporous silicalite-1 shell: Preparation and enhanced catalytic properties in methane co-aromatization with propane

Gas induced surface reconstruction of CuZnSi catalyst for methanol synthesis

The Effects of Silanation of External Acid Sites on the Structure and Catalytic Behavior of Mo/H–ZSM5

Mo/HMCM-22 Catalysts for Methane Dehydro-Aromatization: A Multinuclear MAS NMR Study

Anatase‐reinforced PtZn@Silicalite‐1 Structured Catalysts Boosting Propane Dehydrogenation

Synthesis of hollow HZSM-5 zeolite-based catalysts and catalytic performance in MTA reaction

Fabrication and Catalytic Performance of Mn Loaded Hierarchical Fe-Zsm-5 Zeolite for Chlorobenzene Combustion

Solvent-free Crystallization of ZSM-5 Zeolite on SiC Foam As a Monolith Catalyst for Biofuel Upgrading