In Situ Soft X-ray Spectromicroscopy of Early Tricalcium Silicate Hydration
Sungchul Bae,Manabu Kanematsu,Daniel Hernández-Cruz,Juhyuk Moon,David Kilcoyne,Paulo J. M. Monteiro,Paulo Monteiro
DOI: https://doi.org/10.3390/ma9120976
IF: 3.4
2016-12-01
Materials
Abstract:The understanding and control of early hydration of tricalcium silicate (C₃S) is of great importance to cement science and concrete technology. However, traditional characterization methods are incapable of providing morphological and spectroscopic information about in situ hydration at the nanoscale. Using soft X-ray spectromicroscopy, we report the changes in morphology and molecular structure of C₃S at an early stage of hydration. In situ C₃S hydration in a wet cell, beginning with induction (~1 h) and acceleration (~4 h) periods of up to ~8 h, was studied and compared with ex situ measurements in the deceleration period after 15 h of curing. Analysis of the near-edge X-ray absorption fine structure showed that the Ca binding energy and energy splitting of C₃S changed rapidly in the early age of hydration and exhibited values similar to calcium silicate hydrate (C-S-H). The formation of C-S-H nanoseeds in the C₃S solution and the development of a fibrillar C-S-H morphology on the C₃S surface were visualized. Following this, silicate polymerization accompanied by C-S-H precipitation produced chemical shifts in the peaks of the main Si K edge and in multiple scattering. However, the silicate polymerization process did not significantly affect the Ca binding energy of C-S-H.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering