Superhydrophobic UHMWPE Foams with High Mechanical Robustness and Durability Fabricated by Supercritical CO 2 Foaming
Binbin Sun,Jun Li,Yahao Guo,Heng Li,Hao-Yang Mi,Binbin Dong,Chuntai Liu,Changyu Shen
DOI: https://doi.org/10.1021/acssuschemeng.1c04573
2021-09-07
Abstract:The low durability and stability of superhydrophobic foams and high fabrication costs are the main reasons that limit their practical applications in water remediation and oil recycling. Herein, an extremely superhydrophobic and exceptionally robust foam was developed based on ultrahigh-molecular weight polyethylene (UHMWPE) by supercritical carbon dioxide (scCO2) foaming and subsequent surface modification. The developed foam comprises a highly porous structure decorated with hydrophobic silica nanoparticles and aligned UHMWPE crystallites, constructing a complex micro–nanosized hierarchical morphology, which contributed to an unprecedented water contact angle (WCA) of 162° and a sliding angle of 1°. When used in selective oil absorption and oil/water separation, the foam demonstrated about 100% separation efficiency in repetitive use and even under a vacuum of −70 Kpa due to its high water repellency. More importantly, the foam has outstanding tolerance against mechanical damages such as ultrasonication, bending and twisting, tape peeling, steel wool abrasion, and knife scratching. The surface could maintain the hierarchical structure and a WCA of over 156° after enduring different damages. Moreover, when the surface is clogged, the foam could restore its superhydrophobicity by arbitrary fracturing and cutting, resulting in a theoretically unlimited lifespan. This work not only proposes a UHMWPE-based superhydrophobic foam with extremely high superhydrophobicity, durability, and separation efficiency but also provides insights into the design and mass production of ultraefficient and robust superhydrophobic porous materials for practical applications.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acssuschemeng.1c04573.High-speed video of a 6 μL water droplet impinging the surfaces coated by the original and modified silica NPs with an impacting velocity of 1.08 m/s (MP4)High-speed video of a 6 μL water droplet dropping on the surfaces coated by the original and modified silica NPs with a tilting angle of 3 (MP4)Water droplet adhesion test parallel to the UF-MSU foam surface (AVI)Water droplet adhesion test perpendicular to the UF-MSU foam surface (AVI)UF-MSU was selectively absorbing light and heavy oil from an oil–water mixture (MP4)UF-MSU was selectively pumping light oil from an oil–water mixture (MP4)UF-MSU was selectively pumping heavy oil from an oil–water mixture (MP4)UF-MSU foam abraded using steel wool and impacted by blue-dyed water flow (MP4)UF-MSU foam scratched with a knife and impacted by blue-dyed water flow (MP4)Optimization of foaming conditions, pore size distribution of UF fabricated under optimized conditions, DSC curves of the first heating process of the solid UHMWPE, UF foams and UF foams etched at a different temperature ranging from 40 to 100 °C, SEM image of the internal UFs etched at 100 °C for 1 min, droplet impact test and adhesion test on the surface coated by original silica NPs and MS NPs, SEM images of the UHMWPE powders before and after etching at 100 °C for 30 s, the self-cleaning process of a UF-MSU foam contaminated by sands with a tilting angle of 30°, WCA results of the UF-MSU foam with different PH solutions on the surface, WCA results of the UF-MSU foam stored in an extremely harsh environment, WCA results of the foams after the mechanical stability test, process of blue-dyed water impacting the UF-MSU foam with ultrasonication in ethanol for 1 h, and absorption performance comparison (PDF)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology