Rearranging Low-Dimensional Phase Distribution of Quasi-2D Perovskites for Efficient Sky-Blue Perovskite Light-Emitting Diodes
Peiyuan Pang,Guangrong Jin,Chao Liang,Bingzhe Wang,Wei Xiang,Dengliang Zhang,Jingwei Xu,Wei Hong,Zewen Xiao,Lei Wang,Guichuan Xing,Jiangshan Chen,Dongge Ma
DOI: https://doi.org/10.1021/acsnano.0c03765
IF: 17.1
2020-08-19
ACS Nano
Abstract:Metal halide perovskites have received much attention for their application in light-emitting diodes (LEDs) in the past several years. Rapid progress has been made in efficient green, red, and near-infrared perovskite LEDs. However, the development of blue perovskite LEDs is still lagging far behind. Here, we report efficient sky-blue perovskite LEDs by rearranging low-dimensional phase distribution in quasi-2D perovskites. We incorporated sodium ions into the mixed-Cl/Br quasi-2D perovskites with phenylethylammonium as the organic spacer and cesium lead halide as the inorganic framework. The inclusion of the sodium ion was found to significantly reduce the formation of the <i>n</i> = 1 phase, which was dominated by nonradiative transition, and increase the formation of other small-<i>n</i> phases for efficient exciton energy transfer. By managing the phase distribution, a maximum external quantum efficiency (EQE) of 11.7% was achieved in the sky-blue perovskite LED, with a stable emission peak at 488 nm. Further optimizing the phase distribution and film morphology with Pb content, we demonstrated the sky-blue devices with the average EQE approaching 10%. This strategy of engineering phase distribution of quasi-2D perovskites with a sodium ion could provide a useful way for the fabrication of high-performance blue perovskite LEDs.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.0c03765?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.0c03765</a>.Lifetime parameters for different perovskite films calculated from TRPL decay, summarized performance of perovskite LEDs with different EMLs for comparison, absorption and PL spectra of 3D perovskites with mixed CsCl and CsBr, performance of perovskite LEDs by adding different content of PEABr, calculated formation energies of 2D perovskites, performance of cross-checked devices based on 1.1PbBr<sub>2</sub>, PL spectra of quasi-2D perovskite films with 20% CsBr replacing 20% NaBr, XPS and UPS spectra of perovskite films without and with 20% NaBr, device performance of perovskite LEDs by adding different content of NaBr, SEM and AFM images of different quasi-2D perovskite films, absorption, PL, XRD spectra, and TRPL decay of perovskite films with 1.0 PbBr<sub>2</sub> and 1.1 PbBr<sub>2</sub>, photographs of operating perovskite LEDs and their corresponding EMLs under ultraviolet lamp, device performance of perovskite LEDs with various excess PbBr<sub>2</sub> and 1.1PbBr<sub>2</sub> but different content of NaBr, and stability of EL spectra of perovskite LEDs driven by voltage (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.0c03765/suppl_file/nn0c03765_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology