Abstract:Research on water quenched silicomanganese slag (WQSMS) has primarily focused on grinding it into micro-powder to be used as auxiliary cementitious materials or to synthesize alkali-activated cementitious materials. However, there is a lack of research on utilizing WQSMS as fine aggregates instead of natural aggregates. Although its properties are similar to granulated blast furnace slag (GBFS), most studies investigating the use of GBFS as fine aggregates have mainly focused on mechanical properties rather than microstructure analyses. Meanwhile, to make full use of industrial solid waste, reduce CO2 emissions, and save energy consumption, solid waste cementitious material based on steel slag (SS), desulphurized gypsum (DG), and GBFS, as well as WQSMS as fine aggregate to replace ISO standard sand and washed-out sand (WOS) in various proportions(0%, 25%, 50%, 75%, and 100%) to prepare mortar and concrete, respectively. Analyses of workability, mechanical properties, and microstructure were carried out, and the improvement of mechanical properties of WQSMS was analyzed by SEM-EDS, SEM-BSE, and the microhardness test. The results show that with the increase of WQSMS, the workability of mortar and concrete decreased, while the mechanical strength increased first and then decreased. The mechanical strengths of them reached the peak when the WQSMS addition reached 50%. The flexural and compressive strengths of the mortar increased by 40% and 9.7%, respectively, while the tensile splitting strength and compressive strength of the concrete increased by 11.9% and 3.4%, respectively. The microstructure of the interfacial transition zone(ITZ) was greatly enhanced by WQSMS, which decreased the porosity by 10.49%, decreased the thickness by 27.27%, and increased the microhardness by 11.0%. However, when the content surpasses 50%, the mechanical strength of mortar and concrete declined due to the loose porosity and poor mechanical strength of WQSMS, and there was insufficient cementitious material to fill these holes. Nonetheless, with 100% content, the mortar maintained its high-performance status, with a flexural strength of 8.0 MPa and a compressive strength of 47.9 MPa, and the concrete still fulfilled the specifications of regular concrete C40. Both the fine aggregate and the cementitious material were composed of solid waste, showing potential environmental benefits and interesting green products for future studies.

Multi-scale Characterization and Modeling of Concrete Permeability Containing Recycled Steel Slag Aggregate

Laboratory Evaluation On The Performance Of Porous Asphalt Mixture With Steel Slag For Seasonal Frozen Regions

Mechanical performance, microstructure, and damage model of concrete containing steel slag aggregate

Recycle of steel slag as cementitious material and fine aggregate in concrete: mechanical, durability property and environmental impact

Influence of Steel Slag on Mechanical Properties and Durability of Concrete

Application of Steel Slag as an Aggregate in Concrete Production: A Review

Effect of fillers on the mechanical properties and durability of steel slag concrete

Synergetic recycling of recycled concrete aggregate and waste mussel shell in concrete: Mechanical properties, durability and microstructure

Experimental Study of Mechanical Properties and Theoretical Models for Recycled Fine and Coarse Aggregate Concrete with Steel Fibers

A review of steel slag as a substitute for natural aggregate applied to cement concrete

A review of the application of steel slag in concrete

Preparation and performance of steel slag and recycled brick aggregate modified concrete under the background of solid waste application

Environmental and feasible analysis of recycling steel slag as aggregate treated by silicone resin

TEST AND ANALYSIS OF INFLUENCING FACTORS OF PERMEABILITY COEFFICIENT OF STEEL SLAG POROUS CONCRETE

Influence of the Steel Slag Particle Size on the Mechanical Properties and Microstructure of Concrete

Study on Road Performance of Cement Fly Ash Stabilized Steel Slag-Concrete Recycled Macadam

Electrical conductivity, microstructures, chemical compositions, and systematic multivariable models to evaluate the effect of waste slag smelting (pyrometallurgical) on the compressive strength of concrete

Effect of water quenched silicomanganese slag as fine aggregate on mechanical properties and microstructure characteristics of solid waste-based mortar and concrete

The impact of GGBS and ferrous on the flow of electrical current and compressive strength of concrete

Technical and environmental assessment of sludge-derived slag generated from high temperature slagging co-gasification process as a sustainable construction material

Durability and mechanical behaviors of steel slag powder concrete