Bulk Heterojunction Organic Photoanodes for Enhanced Water Oxidation and Unassisted Solar Water Splitting

Matyas Daboczi,Flurin Eisner,Joel Luke,Shi Wei Yuan,Noof Al Lawati,Jolanda Simone Müller,Ji-Seon Kim,Jenny Nelson,Salvador Eslava

DOI: https://doi.org/10.26434/chemrxiv-2024-vshsx

2024-06-12

Abstract:Polymer donors and non-fullerene acceptors have played an important role as photoactive materials in the development of high-efficiency organic solar cells, and they have immense potential for photoelectrochemical generation of solar fuels such as green hydrogen. However, their use in water-splitting photoelectrodes has been limited by their instability in aqueous environment and recombination losses at the interface with catalysts. Herein, PM6:D18:L8-BO organic photoanodes are presented reaching high photocurrent density over 25 mA cm-2 at +1.23 VRHE and unprecedented, days-long operational stability under solar illumination. This photoelectrochemical performance was achieved by protecting the photoactive layer by a graphite sheet functionalized with earth-abundant NiFeOOH water oxidation catalyst, providing both water resistance and electrical connection between the catalyst and the photoactive layer without any losses. This strategy also enables unassisted solar water splitting with solar-to-hydrogen efficiency of 5% by monolithic tandem organic photoanodes with PM6:D18:L8-BO and PTQ10:GS-ISO photoactive layers. These results pave the way towards high-efficiency, stable and unassisted hydrogen generation by low-cost organic photoelectrochemical cells.

Chemistry

What problem does this paper attempt to address?

The paper primarily aims to address several key issues in the application of organic semiconductors for photoelectrochemical water splitting for hydrogen production:

1. **Increasing photocurrent density (\(j_{ph}\))**: Although high photocurrent densities exceeding 25 mA/cm² can be achieved in organic photovoltaic devices, achieving the same level of photocurrent density in photoelectrochemical water splitting electrodes remains challenging.

2. **Long-term operational stability**: Developing organic photoanode materials that can maintain stability for several days under actual operating conditions.

3. **Reducing electron losses**: Minimizing electron losses between the organic semiconductor and the catalyst, especially during the water splitting reaction, to improve solar-to-fuel conversion efficiency.

4. **Achieving unassisted solar water splitting**: Constructing stable organic photoanodes to achieve efficient solar water splitting without external bias.

To address the above challenges, the research team designed a mixed-structure organic photoanode based on polymer donors (PM6, D18) and non-fullerene acceptors (L8-BO), and utilized a graphite sheet-functionalized earth-abundant nickel-iron oxyhydroxide (NiFeOOH) catalyst protection layer to prevent material degradation in aqueous environments and eliminate most of the electrical losses between the organic semiconductor and the catalyst. The prepared single-junction photoanode achieved a breakthrough photocurrent density exceeding 25 mA/cm² and demonstrated unprecedented operational stability for several days. Additionally, this approach enabled a solar-to-hydrogen conversion efficiency of up to 5% in a two-electrode setup, showcasing its great potential in the field of low-cost, high-stability, and unassisted solar water splitting.