Effect of H3BO3 Modification on the Char Yield of Epoxy Resin and Structure and Property of Epoxy Resin Carbon Foam

Ping Jun YANG,Tie Hu LI,Hao LI,A Lei DANG

DOI: https://doi.org/10.21203/rs.3.rs-3257326/v1

2023-01-01

Abstract:Abstract H3BO3 promotes the removing oxygen-containing functional groups of epoxy resin (EP) and forms B-O-C bond with EP during pyrolysis. Char yield of EP is decided by the chemical crosslinking of EP and H3BO3 and H3BO3 dehydration. The char yield of 0 and 9 wt% H3BO3 modified EP are 19 and 33.4 wt%, respectively. The graphitization degree and grain stacking thickness of EP carbon foam (CF) first decrease and then increase with H3BO3 increase. The graphitization degree of 0, 3, 6, 9 and 12 wt% H3BO3 modified EP CF are 0, 11.6, 0, 0, and 23.2 %, respectively. Furthermore, the ID/IG value of 0, 3, 6, 9, 12 wt% H3BO3 modified EP CF are 0.97, 1.05, 1, 1.1, and 0.89, respectively. For 0 and 3 wt% H3BO3, the bubbles combine easily and form bigger cell size of CF. When the H3BO3 is 6 wt% above, the combination of bubbles become difficult, and decreases cell size of CF. However, the cell size (760 μm) of 12 wt% H3BO3 modified EP CF is the maxim due to H2O foaming. The electrical conductivity of 0 and 3 wt% H3BO3 modified EP CF is 15.56 to 25.94 S/m, respectively, which is decided by the CF carbon graphite structure and its density. The compressive strength of H3BO3 modified EP CF gradually decreases with H3BO3 increase, which is influenced by CF density. The compressive strength (0.6 Mpa) of 12 wt% H3BO3 modified EP CF is much lower than pure EP CF (3.32 MPa).