Abstract:Steel slag is a calcium-rich but hydration-inactive material. Accelerated carbonation is an effective method to activate its reactivity. In this study, a kind of widely available steel slag, basic oxygen furnace slag (BOFS), was used as the sole material for fabricating dry-mixed compacts; the interactions of casting pressure, water to solid (w/s) ratio and carbonation duration were investigated in terms of their effects on CO2 uptake and compressive strength, with the emphasis of finding the parametric interdependence and the optimized parameters. The results suggested that the casting pressure and water addition determined the framework i.e., initial air voids for BOFS activation. The initial air voids inherent in different sample preparation scenarios described the CO2 uptake and strength behavior. It was found that the optimal casting pressure and w/s for BOFS carbonation to achieve the highest compressive strength (45.57 ± 2.10 MPa) and sequestrate considerable amount of CO2 (9.56 wt%) were 15 MPa and 0.13, respectively. Additionally, adopting optimized parameters enabled the exemption of preconditioning and could simplify the curing process at plant setting. It was also highlighted in this study that the maximized density did not correspond to the highest strength since over compactness of the matrix could restrain the CO2 diffusion for carbonation. Also, portlandite, brucite, larnite, tricalcium aluminate, brownmillerite and some amorphous phases were the critical reactive phase towards carbonation while metal oxides and their solid solution were inert. This study provided insight into the development of CO2-activated BOFS-based construction products towards either environment- or property highlighted purposes.

Unveiling the Impact of Carbonation Treatment on BOF Slag Hydration Activity: Formation and Development of the Barrier Layer

The Effects of Carbonation and Hydration on the Mineralogy and Microstructure of Basic Oxygen Furnace Slag Products

Accelerated carbonation and stabilization of BOF slag: data fitting relationship between particle size and CO2 sequestration

Effect of Carbonation Degree on Mineral Composition, Microstructure, and Cementitious Properties of BOF Slag

Mineral Carbonation of Basic Oxygen Furnace Slags

Effect of Direct Carbonation Routes of Basic Oxygen Furnace Slag (BOFS) on Strength and Hydration of Blended Cement Paste

CO2 Sequestration Via Mineralization of Basic Oxygen Furnace Slag

Interdependent factors contributing towards carbonation of steel slag compact: consideration of casting pressure, water dosage and carbonation duration

Carbonation and Utilization of Basic Oxygen Furnace Slag Coupled with Concentrated Water from Electrodeionization

Co-carbonation Behaviors of Blast Furnace Ferronickel Slag-Cement in Aqueous Conditions and the Associated Mechanisms

High-gravity Carbonation of Basic Oxygen Furnace Slag for CO2 Fixation and Utilization in Blended Cement

Impacts of Hydration Degree of Steel Slag on Its Subsequent CO2 Capture Behaviors and Mechanical Performances of Prepared Building Materials

Multiple model approach to evaluation of accelerated carbonation for steelmaking slag in a slurry reactor

Mechanical Activation of Medium Basicity Steel Slag under Dry Condition for Carbonation Curing

Mineral Sequestration of CO2 Using Basic Oxygen Furnace (BOF) Steelmaking Slag

A novel approach to accelerate carbon dioxide sequestration of ladle furnace slag using sodium bicarbonate solution

Use of Carbonation Treatment on Steel Slag for Activity Improvement and Co2 Capture

Accelerated carbonation of ladle furnace slag and characterization of its mineral phase

Effect of Carbonation Treatment on the Properties of Steel Slag Aggregate

Optimization of BOFS High-Gravity Carbonation Technology: Consideration of Theoretical Guidance for Up-scaling Applications

Study on the Carbonation Properties of BOFS with Γ-C2s Blending