Binder Mixture Proportion Optimization and Durability of Three-Dimensional Textile Reinforced Cementitious Composites Via Thermodynamic Modeling and Experimental Analysis

Ke Cao,Qiongfan Xu,Tong Li,Yujie Yang,Huisu Chen,Jian Zhang,Yudong Han

DOI: https://doi.org/10.1016/j.conbuildmat.2024.136883

IF: 7.4

2024-01-01

Construction and Building Materials

Abstract:The relatively low mechanical strength of concrete canvas (CC), one type of three-dimensional textile reinforced cementitious composites (3D TRC) manufactured by a cement powder impregnating process, limits its application in engineering. To achieve the goals of 4 h and 180d compressive strengths greater than 40 MPa and 110 MPa, respectively, the grouting technique is employed in this study to prepare 3D TRC based on modified calcium sulfoaluminate cement (CSA). Thermodynamic modeling is combined with compressive strength experiments to optimize the dosage of calcium sulfate hemihydrate (HH), Li 2 CO 3 and calcium carbonate (CC-). Quantitative X-ray diffraction (QXRD) analysis is used to verify the reliability of the thermodynamic prediction. In addition, the time -dependent compressive strength of 3D TRC with the optimal mix proportions is tested after being exposed to accelerated carbonation of 20 % CO 2 , 5 % NaCl attack, and 5 % MgSO 4 attack. The corresponding aggressive mechanisms are explored via thermodynamic modeling and verified by QXRD analysis. The findings indicate that the 3D TRC with the optimal mixture proportion (CSA: HH: CC- =69:23:8 by mass, 0.05 % Li 2 CO 3 by mass of binder) exhibits the highest 4 h and 180d compressive strengths (45.37 and 112.26 MPa, respectively) and the most effective resistance to chloride attack, but the least resistance to carbonation and sulfate attack. The developed 3D TRC products and the techniques employed in this study could be helpful to widen the application of 3D TRC in civil engineering.