Abstract:Drawing inspiration from the nitrate reductase enzymes, which catalyze nitrate to nitrite in nature, here we introduce a bio-inspired, reduced molybdenum oxide (MoOx) shell that is grown on top of a dendritic nickel foam core (NiNF). The resulting MoOx/NiNF material is prepared via a facile, two-step electrodeposition strategy using commercially available, low-cost precursors. This catalytic material displays a remarkable faradaic efficiency (FE) of 99% at −0.5 V vs. RHE and a high ammonia (NH3) yield rate of up to 4.29 mmol h−1 cm−2 at −1.0 V vs. RHE in neutral media. Most importantly, MoOx/NiNF exhibits exceptional stability for the nitrate reduction reaction (NO3RR), maintaining operation for over 3,100 hours at a high current density of −650 mA cm−2, with a yield rate of 2.6 mmol h−1 cm−2 and a stable average NH3 FE of ~83%. We show, through combined XPS and in-situ Raman spectroscopy, that the pronounced affinity of MoOx/NiNF for nitrate is associated with a substantial presence of oxygen vacancies within the material.

What problem does this paper attempt to address?

This paper mainly discusses how to efficiently reduce nitrate to ammonia using bio-inspired molybdenum oxide (MoOx) electrocatalysts. In this study, the authors prepared a novel MoOx/NiNF material by growing a MoOx shell on a branched nickel foam (NiNF) core. This catalyst was synthesized using a simple two-step electrodeposition strategy and commercial low-cost precursors. Experimental results showed that this catalyst exhibited a Faradaic efficiency (FE) of 99% and a high ammonia (NH3) yield in a neutral medium, reaching up to 4.29 mmol h-1 cm-2. The paper points out that nitrate is a major byproduct of excessive fertilization, posing a threat to the environment and human health. Although electrocatalytic methods have been proposed for denitrification, early work mainly focused on nitrogen gas generation, while selective ammonia production is more challenging due to its involvement in multiple-step reactions and the competing hydrogen evolution reaction. Inspired by nitrate-reducing enzymes in nature, the designed MoOx/NiNF catalyst can promote the activation of nitrate on the Mo center while reducing the competition from the hydrogen evolution reaction, thanks to the presence of oxygen vacancies. Characterization of MoOx/NiNF, including scanning electron microscopy, energy-dispersive X-ray spectroscopy, focused ion beam milling, scanning transmission electron microscopy, and Raman spectroscopy, confirmed the amorphous nature of the MoOx layer and its uniform coverage on the nickel core. In addition, depth-profiling analysis by X-ray photoelectron spectroscopy (XPS) revealed the presence of oxygen vacancy-containing mixed-valence molybdenum oxide surface layer, confirming the core-shell structure of MoOx/NiNF. Under neutral conditions, MoOx/NiNF demonstrated excellent performance in electrocatalytic nitrate reduction reaction (NO3RR) with high ammonia selectivity and low overpotential, maintaining long-term stability at high current densities, with continuous operation for over 3100 hours. These findings are of great significance for the development of catalysts for water denitrification processes.

A Bio-inspired Dendritic MoOx Electrocatalyst for Efficient Electrochemical Nitrate Reduction to Ammonia

A Bio‐Inspired Dendritic MoOx Electrocatalyst for Efficient Electrochemical Nitrate Reduction to Ammonia

A Bio‐Inspired Dendritic MoOx Electrocatalyst for Efficient Electrochemical Nitrate Reduction to Ammonia (Adv. Energy Mater. 37/2024)

Modulation of Charge Distribution Enabling CuNi Nano-Alloys for Efficient Ammonia Oxidation Reaction to Nitrite Production

Molybdenum−Modified Titanium Dioxide Nanotube Arrays as an Efficient Electrode for the Electroreduction of Nitrate to Ammonia

Cu/CuOx In-Plane Heterostructured Nanosheet Arrays with Rich Oxygen Vacancies Enhance Nitrate Electroreduction to Ammonia.

MoC nanocrystals confined in N-doped carbon nanosheets toward highly selective electrocatalytic nitric oxide reduction to ammonia

Atomically Mo-Doped SnO 2-x for efficient nitrate electroreduction to ammonia

High-efficiency electrocatalytic nitrite-to-ammonia conversion on molybdenum doped cobalt oxide nanoarray at ambient conditions

MoO 2 /Ni Heterojunction with Strong Electronic Coupling Prepared by In-situ Phase Separation for High-Efficiency Nitrate Electroreduction to Ammonia

NiMoO 4 nanorods with oxygen vacancies self-supported on Ni foam towards high-efficiency electrocatalytic conversion of nitrite to ammonia

MOF-on-MOF Heterostructured Electrocatalysts for Efficient Nitrate Reduction to Ammonia.

Multi-layer core–shell metal oxide/nitride/carbon and its high-rate electroreduction of nitrate to ammonia

FeMo-N nanosheet arrays supported on nickel foam for efficient electrocatalytic reduction of N2 to NH3 at ambient condition

Understanding the Synergy between Fe and Mo Sites in the Nitrate Reduction Reaction on a Bio-Inspired Bimetallic MXene Electrocatalyst

First principle investigation of nitric oxide reduction reaction for efficient ammonia synthesis over a Fe–Mo dual-atom electrocatalyst

Electroreduction of Nitrate to Ammonia on Palladium–Cobalt–Oxygen Nanowire Arrays

A Bioinspired Iron-Centered Electrocatalyst for Selective Catalytic Reduction of Nitrate to Ammonia

Nickel-cobalt alloy nanosheet-decorated three-dimensional titanium dioxide nanobelts electrodeposited on titanium meshes for boosting selective nitrate electroreduction to ammonia

Regulating RuxMoy Nanoalloys Anchored on Porous Nitrogen-Doped Carbon via Domain-Confined Etching Strategy for Neutral Efficient Ammonia Electrosynthesis

Electrochemical reduction of nitrite to ammonia on amorphous MoO3 nanosheets