MgBu2 Nanosheets Encapsulated in ZIF-8 for Producing Carbon Scaffold in Situ Nanoconfined Mg Hydrogen Storage Materials: Record-high Loading and Decreased Dehydrogenation Enthalpy

Xiaofei Xing,Yuxiang Wang,Zhao Zhang,Mingxing Wei,Xinjia Zhang,Jian Zhou,Zhimei Sun,Tong Liu

DOI: https://doi.org/10.1016/j.nanoen.2024.109740

IF: 17.6

2024-01-01

Nano Energy

Abstract:Nanoconfinement is an effective strategy to improve the kinetic and thermodynamic properties of the Mg/MgH2 2 system. However, current nanoconfinement approaches including porous scaffolds impregnation and surface anchoring can hardly obtain high loading, agglomeration resistant, and air-stable Mg nanoparticles. Herein, we report a novel strategy for preparing carbon scaffold in situ nanoconfined Mg hydrogen storage materials. The 12.2 nm MgBu2 2 nanosheets precipitated by solvent displacement are encapsulated in ZIF-8 to prepare MgBu2@ZIF-8, 2 @ZIF-8, which are then pyrolyzed at 800 degrees C degrees C to obtain Mg@C nanocomposites with 8.7 nm Mg embedded in a carbon scaffold. First principles calculations have demonstrated that the addition of MgBu2 2 promotes the nucleation and growth of ZIF-8 to form MgBu2@ZIF-8. 2 @ZIF-8. It is worth noting that the loading rate of Mg@C-3 sample reaches a record high of 76.3% and exhibits outstanding hydrogen storage performances. Surprisingly, the enthalpy of hydrogen absorption/desorption sharply decreases to-62.0/63.1 kJ mol-1- 1 H2. 2 . Mg@C-3 can absorb 4.4 wt% H2 2 at 200 degrees C degrees C and desorb 4.0 wt% H2 2 at 250 degrees C, degrees C, and the activation energy for hydrogen absorption/ desorption is reduced to a staggering 53.1/74.2 kJ mol-1- 1 H2. 2 . Moreover, Mg@C-3 shows high cycling stability and antioxidant performance. This work opens a novel approach for the development of nanoconfined Mg nanocomposites with excellent performances.