Abstract:Low carbon ferrochrome slag (LCFS) is the metallurgical waste slag from the carbon ferrochrome alloy smelting process. Compared with high carbon ferrochrome slag, LCFS has great potential as cementitious material; the chemical compositions of the two types of slag are quite different. In this research, composite cementitious materials are prepared which use low carbon ferrochrome slag and granulated blast furnace slag (GBFS) as the main raw material. Steel slag mud (SSM) and flue gas desulfurization gypsum (FGDG) are used as the activator. In order to find the variety rule of compressive strength on the composite cementitious materials, a three-factor three-level Box-Behnken design is used to discuss the following independent variables: LCFS content, GBFS content, and water-binder ratio. Moreover, the hydration characteristics of the LCFS-GBFS composite cementitious materials is studied in this paper in terms of hydration product, micromorphology, and hydration degree, based on multi-technical microstructural characterizations. The results show that the compressive strength of the LCFS-GBFS composite cementitious materials is significantly affected by single factors and the interaction of two factors. The mechanical property of the mortar samples at 3, 7, and 28 days are 26.6, 35.3, and 42.7 MPa, respectively, when the LCFS-GBFS-SSM-FGDG ratio is 3:5:1:1 and the water-binder ratio is 0.3. The hydration products of LCFS-GBFS composite cementitious materials are mainly amorphous gels (C-S-H gel), ettringite, and Ca(OH)2. With the increase of LCFS content, more hydration products are generated, and the microstructure of the cementitious system becomes more compact, which contributes to the compressive strength. The results of this research can provide a preliminary theoretical foundation for the development of LCFS-GBFS composite cementitious materials and promote the feasibility of its application in the construction industry. Deep hydration mechanism analysis and engineering applications should be studied in the future.

Effect of W/b Ratio and Supplemental Cementitious Material on the Chloride Penetration and Corrosion Resistance of Ferroaluminate Cement Concrete

Chloride penetration resistance and chloride binding capacity under different application environments of ferroaluminate cement

Exploration of hydration and durability properties of ferroaluminate cement with compare to Portland cement

Improving Corrosion Resistance and Prolonging the Service Life of High-performance Concrete Structures Using Fly Ash and Ground Granulated Blast-furnace Slag

Chloride Resistance and Binding Capacity of Cementitious Materials Containing High Volumes of Fly Ash and Slag

Synergetic Effect of Fly Ash and Ground-Granulated Blast Slag on Improving the Chloride Permeability and Freeze–thaw Resistance of Recycled Aggregate Concrete

Influence of Mineral Admixtures on Compressive Strength, Gas Permeability and Carbonation of High Performance Concrete

Effect of calcium formate on the compressive strength, and hydration process of cement composite containing fly ash and slag

Mechanical Properties and Chloride Penetration Resistance of Concrete Combined with Ground Granulate Blast Furnace Slag and Macro Synthetic Fiber

Durability of Alkali-Activated Fly Ash Concrete: Chloride Penetration in Pastes and Mortars

Effect of decarbonization of high carbon fly ash on workability, mechanical properties and durability of concrete

Alkali-activated concretes based on high unburned carbon content fly ash: carbonation and corrosion performance

Calcined Clay and Limestone as Partial Replacements of Portland Cement: Electrochemical Corrosion Behavior of Low Carbon Steel Rebar as Concrete Reinforcement in Corrosive Environment

Effect of mineral admixtures on the resistance to sulfate attack of reactive powder concrete

Effect of Chloride Ion Corrosion on the Microstructure of Multiple Interfaces of Alkali-Activated GGBS/FA Based Recycled Concrete

Effect of Composite Fibers and Fly Ash on the Properties of Portland–Sulfoaluminate Composite Cement-Based Grouting Sealing Materials

A numerical study on chloride transport in alkali-activated fly ash/slag concretes

How Competitive Hydration between C 3 A and C 3 S in the Fast Dissolution Stage Affects the Hydration of Low-Heat Portland Cement Blended Pastes

Effect of Fly Ash on Frost-Resistance and Chloride Ions Diffusion Properties of Marine Concrete

Preparation and Hydration Mechanisms of Low Carbon Ferrochrome Slag-Granulated Blast Furnace Slag Composite Cementitious Materials

A study of chloride binding capacity of concrete containing supplementary cementitious materials