Sr dope rutile-RuO2 for enhanced Proton exchange membrane electrolyzed water

tianyu wu,jinbo wang,mengyi qiu,yubin jiang,chi song,junyi zheng,ru chen

DOI: https://doi.org/10.26434/chemrxiv-2024-frs38

2024-05-14

Abstract:As an OER catalyst under acidic conditions, Ir has a high cost and poor activity. Ru is the most promising Ir substitute due to its lower cost and higher catalytic activity, and the development of Ir substitutes has become an urgent need. Herein, we have designed and prepared Sr-doped RuO2 to achieve an ultra-low overpotential (197 mV@ 10 mA cm-2).In the PEM single cell, a low pool voltage (1.686 V) was achieved at a current density of 1 A cm-2, together with a high stability retention over 400 h of testing. In addition, the catalytic degradation rates (4.63 ng h-1) were significantly lower than those of commercial RuO2, and the activity is attributed to the increased number of Ru3+ active sites and the very small size (5.10 nm). This work provides a new approach for the development of non-Ir-based catalysts with high activity and stability for acidic oxygen precipitation.

Chemistry

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to develop an efficient and stable catalyst to replace iridium (Ir) for the oxygen evolution reaction (OER) in proton - exchange - membrane water electrolysis (PEMWE). Specifically, the authors designed and prepared a Sr - doped RuO₂ catalyst (Sr - RuO₂) to overcome the problems of insufficient activity and stability of existing Ru - based catalysts in acidic conditions.

### Main problems and background:

1. **Limitations of iridium (Ir) catalysts**:
- As an OER catalyst in acidic conditions, iridium (Ir), although highly active, has high cost and poor stability, which limit its wide application.

2. **Advantages and challenges of ruthenium (Ru) as a substitute**:
- Ruthenium (Ru) is considered the best substitute for iridium because of its lower cost and higher catalytic activity. However, Ru - based catalysts also have problems of insufficient activity and stability, especially in an acidic environment.

3. **Urgent need**:
- The development of high - performance, low - cost, and stable non - iridium - based OER catalysts has become an urgent need, especially in proton - exchange - membrane water electrolysis (PEMWE).

### Solution:

The authors improved the performance of RuO₂ by introducing strontium (Sr) doping. Specifically, Sr - RuO₂ exhibits the following advantages:
- **Ultra - low overpotential**: At a current density of 10 mA cm⁻², the overpotential is only 197 mV.
- **Low cell voltage**: In a PEM single - cell, at a current density of 1 A cm⁻², the cell voltage is only 1.686 V.
- **High stability**: It shows excellent stability in a 400 - hour test.
- **Low catalytic degradation rate**: The catalytic degradation rate is 4.63 ng h⁻¹, much lower than that of commercial RuO₂.

### Conclusion:

Through Sr doping, the catalytic performance of RuO₂ has been significantly improved. In particular, the increase in Ru³⁺ active sites and the decrease in nanoparticle size make Sr - RuO₂ a promising non - iridium - based OER catalyst suitable for proton - exchange - membrane water electrolysis in an acidic environment.