Abstract:The MnOx-CeO2 metal oxides are considered as promising alternative catalysts for selective catalytic reduction with NH3 (NH3-SCR) to remove NOx due to its excellent low-temperature performance. However, their strong oxidative ability can lead to NH3 over-oxidation, narrowing the active temperature range and reducing N2 selectivity. Moreover, their weak surface acidity hampers medium to high-temperature activity and alkali metal resistance. Hence, in this study, MnCeOx metal oxides were coupled with HY zeolite to create MnCeOx/HY, demonstrating excellent NH3-SCR performance. The high dispersion of metal oxides on the zeolite surface and their close integration promoted strong electron interaction, effectively reducing oxygen vacancies and surface adsorbed oxygen concentrations. Consequently, the oxidative ability of active metal oxides was appropriately weakened, suppressing undesirable side reactions. MnCeOx/HY also notably suppressed NO adsorption and nitrate formation, promoting the catalytic reaction solely through the E-R mechanism and enhancing N2 selectivity. The abundant strong acid sites on the zeolite surface facilitates NH3 adsorption at moderate to high temperatures, notably expanding the active temperature window. Furthermore, the acid sites of HY zeolite serve as sacrificial sites, preferentially reacting with alkali metals, thus exhibiting excellent resistance to alkali metal poisoning on MnCeOx/HY. Combining with the DFT results, the structure-activity relationships in this study also reveal the importance of the effective synergy between acid sites and redox sites for optimal catalytic performance, offering valuable insights into the development of highly active and alkali-resistant denitrification catalysts.

CaMnO3 Perovskite-Derived Porous Γ-Mno2 for Highly Efficient Oxidation of NH3 and NO

Sulfur-resistant Catalytic NO Oxidation over Surface-Disproportionated CaMnO3 Perovskites

Promoting Metal Oxides–zeolite Electron Interaction on MnCeOx/HY Catalyst for Boosting Nitrogen Oxides Reduction

Constructing Γ-Mno2 with Abundant Oxygen Vacancies by a Chelating Agent-Assistant Strategy to Achieve High-Efficient Conversion of NO to NO2

Porous MnOx for Low-Temperature NH3-SCR of NOx: the Intrinsic Relationship Between Surface Physicochemical Property and Catalytic Activity

Taming NO oxidation efficiency by γ-MnO2 morphology regulation

Synthesis, characterization and catalytic performances of Cu- and Mn-containing ordered mesoporous carbons for the selective catalytic reduction of NO with NH3

Nitrogen Promoted Electron Transfer to Create Highly Active Cu2+ and Mn3+ Sites for Efficient Catalytic Ozonation of Ammonia over Copper and Nitrogen Co-Doped Cryptomelane-Type Manganese Oxide at Ambient Temperature

Molybdenum-containing oxide catalysts for selective catalytic reduction of NOx with NH3

The fabrication of Mn single atoms/clusters on Al2O3 for enhanced catalytic NO oxidation

Performance of Modified La Xsr1- Xmno3 Perovskite Catalysts for NH3 Oxidation: TPD, DFT, and Kinetic Studies.

MnOx Fabrication with Rational Design of Morphology for Enhanced Activity in NO Oxidation and SO2 Resistance

Abundant Oxygen Vacancies Induced by the Mechanochemical Process Boost the Low-Temperature Catalytic Performance of MnO2 in NH3-SCR

A simple hydrothermal synthesis of oxygen vacancy-rich MnMoO4 rod-like materials and its highly efficient electrocatalytic nitrogen reduction

Preparation of Cr-Mn Mixed Oxide by Coprecipitation and Its Performance for Low-Temperature Selective Catalytic Reduction of NOx

Mesostructured amorphous manganese oxides: facile synthesis and highly durable elimination of low-concentration NO at room temperature in air.

Low-temperature selective catalytic reduction of NOx with NH3 over in-situ grown MnOx-Fe2O3/TiO2/Ti monolithic catalyst

A Simple Hydrothermal Synthesis of an Oxygen Vacancy-Rich MnMoO4 Rod-Like Material and Its Highly Efficient Electrocatalytic Nitrogen Reduction.

MnyCo3−yOx Bimetallic Oxide Prepared by Ultrasonic Technology for Significantly Improved Catalytic Performance in the Reduction of NOx with NH3

Electrocatalytic nitrite conversion to ammonia over Mn single atoms anchored on MoO 3-x

Catalytic oxidation of NO over SmMn2O5 nanostructures derived from different Mn precursors