Intermetallic particles distribution in 7XXX series aluminium alloy substrate impacts cathodic stability of silicate sealed anodized oxide

Polina Volovitch,Florian Raffin,Maxime Magnan,Antoine Seyeux,Sandrine Zanna,Jaques Echouard,Jolanta Światowska
DOI: https://doi.org/10.26434/chemrxiv-2024-g70d0
2024-05-03
Abstract:A silicate sealing on two tartaric sulphuric acid anodized 7XXX-series aluminium alloys was studied. SEM-EDS, XPS, ToF-SIMS, GDOES, and Raman spectroscopy demonstrated similar morphology and chemical composition of all the sealed layers. Electrochemistry coupled with time-lapse microscopy evidenced that the layers, although stable under anodic polarization, demonstrated localized pitting of the oxide under cathodic polarization in Cl-containing electrolyte. No chemical or morphological surface modification was detected outside of the pits. The number and size of the pits depended on the IMPs distribution in the alloy, buried under 6 µm thick oxide. A degradation mechanism explaining these observations was proposed.
Chemistry
What problem does this paper attempt to address?
This paper mainly discusses the changes in the corrosion resistance of 7XXX series aluminum alloys (rich in zinc, magnesium, and copper) after surface treatments, especially anodizing and silicate sealing treatment. The study found that although the sealing layer is stable under anodic polarization, local pitting corrosion occurs under cathodic polarization in electrolytes containing chloride ions. The quantity and size of the pits are related to the distribution of intermetallic particles (IMPs) in the alloy matrix, which are buried under a 6-micrometer-thick oxide layer. The paper proposes a possible degradation mechanism and conducts experiments on 7010-T7451 and 7175-T6 alloys treated with different concentrations of alkaline silicate sealants under two different processes (machining and rolling) to study how alloy processing affects the stability of the sealing layer. The research methods include electrochemical tests, microscopic observations, and spectroscopic analysis, aiming to evaluate the specific impact of IMPs distribution on the cathodic stability of silicate-sealed anodized layers.