Aramid Nanofiber‐Based Artificial Nacre‐Supported Graphene/Silver Nanowire Nanopapers for Electromagnetic Interference Shielding and Thermal Management

Fugang Hu,Ningfeng Gong,Jinsong Zeng,Pengfei Li,Tianguang Wang,Jinpeng Li,Bin Wang,Kefu Chen

DOI: https://doi.org/10.1002/adfm.202405016

IF: 19

2024-01-01

Advanced Functional Materials

Abstract:The development of next-generation flexible electronics hinges on the creation of materials that are not only mechanically robust but also multifunctional. Herein, a novel approach is presented to fabricate an aramid nanofibers/cellulose nanocrystals/montmorillonite nanoplates (ACM) composite substrate with a robust "brick and mortar" microstructure. This substrate is seamlessly integrated with a high-performance graphene/silver nanowire (G/Ag) composite conductive layer, resulting in the creation of ACM&G/Ag nanopapers. The resulting nanopapers achieve remarkable tensile strength (delta(c)) (543.82 MPa), tensile modulus (E-c) (10.93 GPa), and toughness (U-c) (95.18 MJ m(-3)). Notably, when normalized by weight, the specific tensile strength of these nanopapers surpasses that of commercial titanium alloy, reaching 399.87 MPa g(-1) cm(3), compared to titanium alloy's 257.00 MPa g(-1) cm(3). With a high conductivity of 1398.08 S cm(-1), ACM&G/Ag nanopapers exhibit impressive electromagnetic interference shielding effectiveness (EMI SE) of 39.59 dB and EMI SE/t of 16359.26 dB cm(-1). Moreover, ACM&G/Ag nanopapers exhibit exceptional thermal management performance, featuring high electrical heating temperature (280 degrees C), rapid response time (<6 s), enduring heating stability, deicing capacity, and reliable heating performance even in humid environments. These results underscore the substantial potential of these high-performance nanopapers in diverse applications such as wearable devices, electromagnetic compatibility, thermal management, human health, and aerospace.