Abstract:Microstructure characteristics are important for the high-performance Sm2Co17-type permanent magnets to achieve high intrinsic coercivity (H cj) and large magnetic field at the knee-point (H knee). In this work, the correlation between microstructures and magnetic properties has been systematically studied. The different microstructures were obtained by two procedures: by adjusting the aging temperature and optimizing the Zr content. On one hand, with increase of aging temperature from 1063 K to 1103 K, the cell size and the lamellar phase density increase from 75.1 nm and 0.014 1/nm to 101.5 nm and 0.043 1/nm, respectively, and the average peak Cu concentration at the cell boundaries reaches 21.9 at% which is helpful for obtaining relatively high H cj and H knee. As the aging temperature increases further to 1143 K, a much larger cell size and with incomplete cell boundaries results in an irregular distribution of Cu concentration at the cell boundaries. In this case, the H knee is low even though the magnet shows a high H cj. On the other hand, the increase of Zr content also promotes an increase in both the lamellar phase density and the average peak Cu concentration at the cell boundaries, giving rise to high H cj and H knee. Taking into consideration the aging temperature and Zr content, one can conclude that a lower aging temperature and lower Zr content produce a lower lamellar phase density and average Cu concentration at the cell boundaries and this leads to a lower H cj and H knee of the magnets. To further confirm this correlation between the microstructures and magnetic properties, a magnet of Sm(CobalCu0.062Fe0.285Zr0.016)7.6 was aged at a higher temperature of 1143 K to increase the lamellar phase density. As expected, the lamellar phase density increases from 0.008 to 0.013 1/nm; however, the cell size increases simultaneously from 142.5 to 247 nm. The magnet exhibits a much higher but uneven Cu concentration at the cell boundaries. As a result, the H cj increases from 1.64 to 10.18 kOe, while H knee just increases from 1.09 to 3.91 kOe.

In Situ High-Temperature Transmission Electron Microscopy Investigation of Dynamic Element Migration for Sm-Co-Fe-Cu-Zr Sintered Magnets

Effect of interfacial stress on microchemistry and coercivity in 2:17-type SmCo sintered magnets

Temperature dependence of magnetization processes in Sm(Co,Fe,Cu,Zr)$_z$ magnets with different nanoscale microstructures

Microstructure characteristics and optimization of 2:17-type Sm-Co sintered magnets with different iron content

Quantitative analysis of pinning-hardened intrinsic coercivity of Sm(CoFeCuZr)z (z = 7.0–7.8) high-temperature permanent magnets

Effect of Ingot Cooling Rate on Cu Distribution and Magnetic Properties of Sm(CobalFe0.28Cu0.07Zr0.03)7.6 Magnets

Phase separation and chemistry evolution in Fe-rich Sm(CobalFe0.31Cu0.07Zr0.025)7.7 magnets: The effect of initial defect

Improvement of coercivity thermal stability of sintered 2:17 SmCo permanent magnet by Nd doping

Temperature-dependent microstructure and magnetic properties evolution in the sintered Nd-Fe-B magnets with Pr-Al-Cu diffusion

Influence of the final heat treatment temperature on the magnetic property losses of Sm(Co,Fe,Cu,Zr)z high temperature magnets

Influence of 1:7 H phase stability on the evolution of cellular microstructure in Fe-rich Sm-Co-Fe-Cu-Zr magnets

Long Term Aging-Induced Microstructure and Magnetic Performance Changes in Sm-Co-Fe-Cu-Zr Magnets

Effect of post-solutionizing cooling rate on microstructure and magnetic properties of 2:17-type Sm-Co-Fe-Cu-Zr magnets

Overview of composition and technique process study on 2:17-type Sm–Co high-temperature permanent magnet

Study on the grain growth and the evolution of defects around grain boundaries during heat treatment process in Sm 2 Co 17 permanent magnets

In-situ High-Energy X-ray Diffraction Study of the Early-Stage Decomposition in 2:17-Type Sm-Co-based Permanent Magnets

Enhanced Magnetic Properties of Fe-rich Sm-Co-Fe-Cu-Zr Magnets by Compressive Stress-Aging

Phase Separation and Chemistry Evolution in Fe-Rich Sm(Co Balfe 0.31cu 0.07zr 0.025) 7.7 Magnets: the Effect of Initial Defect

Prolonged ordering process induced higher segregation of copper in 2:17 type SmCo magnets

THE INSITU AND DYNAMIC OBSERVATION OF SMCO5 MAGNET AND THE REVERSIBLE VARIATION OF ITS COERCIVITY

Dependence of macromagnetic properties on the microstructure in high-performance Sm2Co17-type permanent magnets