Zn, Co, and Fe Tridoped N–C Core–Shell Nanocages as the High-Efficiency Oxygen Reduction Reaction Electrocatalyst in Zinc–Air Batteries
Guang Li,Wenhui Deng,Li He,Jinyang Wu,Junchang Liu,Tianjing Wu,Ying Wang,Xianyou Wang
DOI: https://doi.org/10.1021/acsami.1c06750
2021-06-09
Abstract:Transition metal–nitrogen–carbon (TM–N–C) nanomaterials are promising platinum-based substitutes for the oxygen reduction reaction (ORR). However, large-scale commercial production of high-efficiency, durable TM–N–C catalysts remains a formidable challenge. In this work, a facile ″ZIF-on-ZIF″ strategy is first adopted to design core–shell polyhedral nanocages, and then, ferrocene (Fc) is added to form @Fc double-layer encapsulating polyhedral nanocages. Finally, Zn, Co, and Fe tridoped N–C nanocages (ZnCoFe–N–C) as the high-efficiency ORR electrocatalyst are prepared through high-temperature annealing. Benefiting from the trimetal, nitrogen and carbon species bond to each other to form highly efficient active sites, and the material exhibits outstanding performance in 0.1 M KOH, onset potential and half-wave potential of up to 0.95 and 0.878 V (vs RHE), respectively, and long-term durability and methanol tolerance. Furthermore, when utilizing as a zinc–air battery (ZAB) air electrode, it exhibits wonderful indicators, reflected in an open circuit voltage of 1.525 V, power density of 350.2 mW cm<sup>–2</sup>, and specific capacity of 794.7 mAh g<sub>zn</sub><sup>–1</sup>, which outperforms the benchmark Pt/C catalyst. This work provides a facile and effective strategy to obtain a highly efficient and stable TM–N–C electrocatalyst for the ORR in ZABs.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c06750?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c06750</a>.Experimental section, supplementary figures, and supplementary tables; synthesis of all samples, materials characterization, and electrochemical measurements; SEM image of uncarbonized precursors and ZnFe–N–C; HRTEM image of ZnCoFe–N–C; XRD analysis of uncarbonized precursors; XPS full scan of all samples and high-resolution spectra of the corresponding samples; N<sub>2</sub> adsorption–desorption isotherm of all catalysts and the pore size distribution; LSV polarization curve of the catalyst at different rotation speeds; chronoamperometric test; RDE polarization curves of all samples in acidic and neutral solutions; power density polarization curve; and elemental content of all samples (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c06750/suppl_file/am1c06750_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology