Abstract:Supercapacitors that can withstand extremely low temperatures have become desirable in applications including portable electronic devices, hybrid electric vehicles, and renewable energy conversion systems. Graphene is considered as a promising electrode material for supercapacitors owing to its high specific surface area (up to 2675 m(2).g(-1)) and electrical conductivity (approximately 2 x 10(2) S.m(-1)). However, the restacking of graphene sheets decreases the accessible surface area, reduces the ion diffusion rate and prolongs the ion transport pathways, thereby limiting the energy storage performance at low temperatures (typically < 100 F.g(-1) at sub-zero temperatures). Herein, we fabricate a supercapacitor based on holey graphene and mixed-solvent organic electrolyte for ultra-low-temperature applications (e.g., -60 degrees C). Reduced holey graphene oxide (rHGO) was synthesized as the electrode material via an oxidative-etching process with H2O2. Methyl formate was mixed with propylene carbonate to improve the electrolyte conductivity at temperatures ranging from -60 to 25 degrees C. The as-fabricated supercapacitor showed a high room-temperature capacitance of 150.5 F.g(-1) at 1 A.g(-1), which was almost 1.5 times greater than that of the supercapacitor using untreated reduced graphene oxide (rGO; 101.4 F.g(-1)). The improved capacitance could be attributed to the increased accessible surface rendered by the abundant mesopores and macropores on the holey surface. As the temperature decreased to -60 degrees C, the rHGO supercapacitor still delivered a high capacitance of 106.2 F.g(-1) with a retention of 70.6%, which was superior to other state-of-the-art graphene-based supercapacitors. Electrochemical impedance spectra tests revealed that the ion diffusion resistance in rHGO was significantly smaller than that in rGO and less influenced by temperature with a lower activation energy. This was because the holey morphology can provide transport pathways for ions and reduce the ion diffusion length during charging/discharging, consequently diminishing the diffusion resistance at low temperatures. Specifically, at -60 degrees C, the energy density of supercapacitor reached up to 26.9 Wh.kg(-1) at 1 A.g(-1) with a maximum power density of 18.7 kW.kg(-1) at 20 A.g(-1), surpassing the low-temperature performance of conventional carbon-based supercapacitors. Moreover, after 10000 cycles at -60 degrees C with a current density of 5 A.g(-1), 89.1% of capacitance was retained, suggesting the stable and reliable power output of the current supercapacitor at extremely low temperatures.

Remarkable Electrochemical Performance of Holey MXene/graphene Hydrogel-Based Supercapacitor Operated at − 60 °C in Sulfuric Acid Aqueous Electrolyte

Hydrogen Bond Crosslinking Hydrogel for High-Performance Ultra-Low Temperature MXene-Based Solid State Supercapacitors

A Supercapacitor Architecture for Extreme Low‐Temperature Operation Featuring MXene/Carbon Nanotube Electrodes with Vertically Aligned Channels and a Novel Freeze‐Resistant Electrolyte

Supercapacitors Based on Low-Temperature Partially Exfoliated and Reduced Graphite Oxide

Ultra-Low-Temperature Supercapacitor Based on Holey Graphene and Mixed-Solvent Organic Electrolyte

MXene-based film electrode and all-round hydrogel electrolyte for flexible all-solid supercapacitor with extremely low working temperature

A Nitrogen-Doped Mesopore-Dominated Carbon Electrode Allied with Anti-Freezing EMIBF4–GBL Electrolyte for Superior Low-Temperature Supercapacitors

A flexible supercapacitor with high capacitance retention at an ultra-low temperature of -65.0°C

A mechanically robust all-solid-state supercapacitor based on a highly conductive double-network hydrogel electrolyte and Ti 3 C 2 T x MXene electrode with anti-freezing property

Modulating Electrolyte Solvation Structure for High‐Voltage and Low‐Temperature Magnesium‐ion Supercapacitors

Concentrated Hydrogel Electrolyte for Integrated Supercapacitor with High Capacitance at Subzero Temperature

Antifreezing Proton Zwitterionic Hydrogel Electrolyte via Ionic Hopping and Grotthuss Transport Mechanism toward Solid Supercapacitor Working at −50 °C

Low‐Temperature and High‐Voltage‐Tolerant Zinc‐Ion Hybrid Supercapacitor Based on a Hydrogel Electrolyte

Boosting PEDOT energy storage with redox anthraquinone dopant for flexible hydrogel supercapacitor under sub-zero temperatures

A low-cost dilute aqueous hybrid electrolyte for low-temperature supercapacitors

Low Temperature Electrochemical Properties and Energy Storage Mechanisms of Gently Modified Porous Carbon Fabric-Based Flexible Supercapacitors

An aqueous magnesium-ion hybrid supercapacitor operated at −50 °C

Accelerated Ion-Desolvation/Diffusion Kinetics and Excellent Anti-Corrosion Capability Enabling Ultrawide-Temperature (–70∼100°C) Supercapacitor

Flexible and Anti-Freezing Quasi-Solid-state Magnesium-Ion Hybrid Supercapacitor Working at -40 °C

An effective 'salt in dimethyl sulfoxide/water' electrolyte enables high-voltage supercapacitor operated at −50 °C

High‐Entropy Electrolyte Design for Low‐Temperature Supercapacitors