Removal of toluene over bi-metallic Pt–Pd-SBA-15 catalysts: Kinetic and mechanistic study

Mulan Chang,Xin Liu,Ping Ning,Qiulin Zhang,Futing Xia,Huimin Wang,Guangcheng Wei,Junjie Wen,Mo Liu,Jia Hu,Tong Tang
DOI: https://doi.org/10.1016/j.micromeso.2020.110111
IF: 5.876
2020-08-01
Microporous and Mesoporous Materials
Abstract:<p>A series of bi-metallic Pt–Pd-SBA-15 catalysts which promoted the dispersion of Pt–Pd by surface functionalization of SBA-15 were prepared and applied for toluene oxidation. We found that PVP-assisted Pt–Pd-SBA-15 exhibited the minimal average particle size (4.6 nm) and the highest Pt<sup>0</sup>/Pt<sup>n+</sup> (50.6%) among the all catalysts decorated with polyvinylpyrrolidon (PVP), citric acid and ethylenediamine, respectively. Kinetic study revealed that the Ea of all catalysts decreased accompanied with catalytic activity in the following order: Pt–Pd-SBA-15-PVP (83.5 kJ/mol) &lt; Pt–Pd-SBA-15-citric (100.1 kJ/mol) &lt; Pt–Pd/SBA-15 (110.7 kJ/mol) &lt; Pt–Pd-SBA-15-(en)<sub>2</sub> (150.6 kJ/mol). Based on the above analyses, a conclusion could be drawn that PVP-induced dispersion process improved significantly the surface Pt<sup>0</sup>/Pt<sup>n+</sup> (50.6%) and reduced the particle size of Pt–Pd nanoparticles, which enhanced the activity of toluene oxidation. Furthermore, In-situ DRIFTS studies showed that benzoic acid and maleic acid were typical intermediates produced during the catalytic combustion of toluene. Wherein, toluene could be oxidized to benzoic acid by positively charged Pt and Pd in the absence of O<sub>2</sub>. On the other hand, toluene was oxidized to maleic acid under an aerobic atmosphere.</p>
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology, applied
What problem does this paper attempt to address?
The problem that this paper aims to solve is to improve the catalytic activity of toluene oxidation through the bimetallic Pt - Pd - SBA - 15 catalyst modified by surface functionalization. Specifically, the researchers hope to prepare bimetallic Pt - Pd catalysts on the SBA - 15 support by using different additives (such as polyvinylpyrrolidone (PVP), citric acid, and ethylenediamine) to promote the dispersion of precious metals, thereby improving the catalytic performance of the catalyst for toluene oxidation. In addition, the paper also explores the influence of different additives on the activity of the catalyst, and analyzes the reaction mechanism through kinetic studies and in - situ DRIFTS technology. ### Main research contents: 1. **Catalyst preparation**: - A series of bimetallic Pt - Pd - SBA - 15 catalysts were prepared by the impregnation method using PVP, citric acid, and ethylenediamine as additives. - The size and distribution of precious metal particles were controlled by different additives to improve the activity of the catalyst. 2. **Catalyst characterization**: - The structure and morphology of the catalyst were characterized by means of N2 adsorption - desorption tests, X - ray diffraction (XRD), transmission electron microscopy (TEM), and scanning transmission electron microscopy (STEM). - The atomic ratio and chemical state on the surface of the catalyst were analyzed by X - ray photoelectron spectroscopy (XPS). 3. **Catalytic performance test**: - The catalytic activity of the catalyst for toluene oxidation was evaluated in a fixed - bed reactor, and the performance of the catalyst was evaluated by measuring the toluene conversion rate at different temperatures. - The activation energy (Ea) of different catalysts was calculated to further understand the activity differences of the catalysts. 4. **Kinetic study**: - The activation energy (Ea) of different catalysts was calculated through kinetic experiments, and it was found that the catalyst with PVP as an additive had the lowest activation energy, indicating that it had the highest catalytic activity for toluene oxidation. 5. **In - situ DRIFTS study**: - The intermediate products generated during the toluene oxidation process were monitored by in - situ DRIFTS technology, and it was found that benzoic acid and maleic acid were typical intermediate products. ### Conclusions: - The Pt - Pd - SBA - 15 catalyst with PVP as an additive exhibited the smallest average particle size (4.6 nm) and the highest surface Pt0/Ptn+ ratio (50.6%), which significantly improved the catalytic activity of toluene oxidation. - Kinetic studies showed that the catalyst with PVP as an additive had the lowest activation energy (83.5 kJ/mol), indicating that it had the strongest activation ability for toluene. - In - situ DRIFTS analysis showed that benzoic acid and maleic acid were typical intermediate products in the catalytic combustion process of toluene. In summary, this study successfully improved the catalytic performance of the bimetallic Pt - Pd - SBA - 15 catalyst for toluene oxidation through surface functionalization modification, providing new ideas for the efficient treatment of volatile organic compounds (VOCs).