Rapid Antibacterial Effects of Silk Fabric Constructed through Enzymatic Grafting of Modified PEI and AgNP Deposition
Feiyu Wang,Biaobiao Yan,Zirong Li,Ping Wang,Man Zhou,Yuanyuan Yu,Jiugang Yuan,Li Cui,Qiang Wang
DOI: https://doi.org/10.1021/acsami.1c08119
2021-07-12
Abstract:Enzymatic antibacterial finishing is an eco-friendly alternative to develop functional silk-based materials. However, the low accessibility of tyrosine residues distributed in fibroin chains restricts the laccase-mediated functionalization of silk fibers (SF). To address this issue, a highly reactive <i>p</i>-hydroxyphenylacetic acid-modified polyethyleneimine (mPEI) was enzymatically grafted onto fibroin using laccase, aiming at constructing an antibacterial matrix of mPEI on the fiber surface. Subsequently, in situ deposition of silver nanoparticles (i.e., AgNPs) into the newly built mPEI network was performed to form a rapid antibacterial layer. The results indicated that laccase efficiently catalyzes the mPEI coupling, the zeta potential of SF-<i>g</i>-mPEI increases from −32 to 21.70 mV, and the silver content reaches 1.81% after AgNP embedment. Based on the combined two-step treatments, the obtained silk fabric exhibited excellent antibacterial abilities against two bacteria, including <i>Staphylococcus aureus</i> (<i>S. aureus</i>) and <i>Escherichia coli</i> (<i>E. coli</i>). The antibacterial rates of both bacteria reached 99.9% within 30 min of contact, remaining over 99.9% within 18 h of contact even after washing 10 times. The present work provides an enzyme-mediated method for construction of silk fabric with durable and rapid antibacterial activity.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c08119?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c08119</a>.Reaction pathway of the laccase-catalyzed grafting of modified-PEI (mPEI) on SF (A, B), and the laccase-assisted self-cross-linking of mPEI (C) (Figure S1), color appearance of the mixture of mPEI and silver ions after incubation at different temperatures (Figure S2), crystalline structures of silk fabrics with different treatments (Figure S3), ATR-FTIR spectra of silk fabrics with different treatments (Figure S4), effects of pH, incubation time, and AgNO<sub>3</sub> concentration on the colorimetric data (L*, a*, and b*) of AgNP-deposited silk fabrics (Table S1) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c08119/suppl_file/am1c08119_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology