Abstract:Integrative osteochondral repair is a useful strategy for cartilage-defect repair. To mimic the microenvironment, it is necessary that scaffolds effectively mimic the extracellular matrix of natural cartilage and subchondral bone. In this study, biomimetic osteochondral scaffolds containing an oriented cartilage layer, a compact layer, and a three-dimensional (3D)-printed core-sheath structured-bone layer were developed. The oriented cartilage layer was designed to mimic the structural and material characteristics of native cartilage tissue and was fabricated with cartilage matrix-chitosan materials, using thermal-induced phase-separation technology. The 3D-printed core-sheath structured-bone layer was fabricated with poly(L-lactide-co-glycolide)/β-tricalcium phosphate-collagen materials by low-temperature deposition technology, using a specially designed core-sheath nozzle, and was designed to mimic the mechanical characteristics of subchondral bone and improve scaffold hydrophilicity. The compact layer was designed to mimic the calcified-layer structure of natural cartilage to ensure the presence of different suitable microenvironments for the regeneration of bone and cartilage. A dissolving-bonding process was developed to effectively combine the three parts together, after which the bone and cartilage scaffolds exhibited good mechanical properties and hydrophilicity. Additionally, goat autologous bone mesenchymal stem cells (BMSCs) were isolated and then seeded into the bone and cartilage layers, respectively, and following a 1 week culture in vitro, the BMSC-scaffold constructs were implanted into a goat articular-defect model. Our results indicated that the scaffolds exhibited good biocompatibility, and 24 weeks after implantation, the femoral condyle surface was relatively flat and consisted of a large quantity of hyaloid cartilage. Furthermore, histological staining revealed regenerated trabecular bone formed in the subchondral bone-defect area. These results provided a new method to fabricate biomimetic osteochondral scaffolds and demonstrated their effectiveness for future clinical applications in cartilage-defect repair.

Trilayered Biomimetic Hydrogel Scaffolds with Dual-Differential Microenvironment for Articular Osteochondral Defect Repair

3D Printing of Biomimetic Multi-Layered GelMA/nHA Scaffold for Osteochondral Defect Repair

A biomimetic bi-layered tissue engineering scaffolds for osteochondral defects repair

Biomimetic injectable and bilayered hydrogel scaffold based on collagen and chondroitin sulfate for the repair of osteochondral defects

Repair of Articular Osteochondral Defects Using an Integrated and Biomimetic Trilayered Scaffold.

Biomimetic Design and Fabrication of Multilayered Osteochondral Scaffolds by Low-Temperature Deposition Manufacturing and Thermal-Induced Phase-Separation Techniques

Bionic Biphasic Composite Scaffolds with Osteochondrogenic Factors for Regeneration of Full-Thickness Osteochondral Defects

Bilayered Scaffold Prepared from a Kartogenin-Loaded Hydrogel and BMP-2-Derived Peptide-Loaded Porous Nanofibrous Scaffold for Osteochondral Defect Repair

Biphasic Double-Network Hydrogel With Compartmentalized Loading of Bioactive Glass for Osteochondral Defect Repair

Biomimetic cartilage scaffold with orientated porous structure of two factors for cartilage repair of knee osteoarthritis

Repair of osteochondral defects mediated by double-layer scaffolds with natural osteochondral-biomimetic microenvironment and interface

Development of Tri‐Layered Biomimetic Atelocollagen Scaffolds with Interfaces for Osteochondral Tissue Engineering

Bi-Layered Composite Scaffold For Repair Of The Osteochondral Defects

Biphasic CK2.1-coated Β-Glycerophosphate Chitosan/ll37-Modified Layered Double Hydroxide Chitosan Composite Scaffolds Enhance Coordinated Hyaline Cartilage and Subchondral Bone Regeneration

Heterogenous Hydrogel Mimicking the Osteochondral ECM Applied to Tissue Regeneration.

Patient-specific Scaffolds with a Biomimetic Gradient Environment for Articular Cartilage-Subchondral Bone Regeneration.

Osteogenesis and Chondrogenesis of Biomimetic Integrated Porous Pva/Gel/V-N-Ha/Pa6 Scaffolds and Bmscs Construct in Repair of Articular Osteochondral Defect

Hyaluronic acid-based biphasic scaffold with layer-specific induction capacity for osteochondral defect regeneration

Preparation and characterization of biomimetic gradient multi-layer cell-laden scaffolds for osteochondral integrated repair

Full-thickness osteochondral defect repair using a biodegradable bilayered scaffold of porous zinc and chondroitin sulfate hydrogel

A bionic composite hydrogel with dual regulatory functions for the osteochondral repair