Structure and Performance of N-Doped Amorphous Carbon Films (A-C: N) on Stainless Steel Surfaces for Bipolar Plates in Proton Exchange Membrane Fuel Cells

Chunling Li,Zijin Liu,Lunlin Shang,Xiaodong He,Xiaoze Yue,Yu Jin,Xinxin Liu,Guangan Zhang

DOI: https://doi.org/10.1016/j.diamond.2024.111387

IF: 3.806

2024-01-01

Diamond and Related Materials

Abstract:Stainless steel bipolar plates (BPPs) are anticipated to supersede traditional graphite BPPs in proton exchange membrane fuel cells (PEMFCs) owing to their superior machinability, enhanced mechanical strength, and cost-effectiveness. Nevertheless, stainless steel BPPs are susceptible to corrosion and dissolution in acidic environments over extended periods, leading to the formation of a passivation film that diminishes conductivity. In this study, amorphous carbon (a-C) films with varying N doping contents were deposited onto 304L stainless steel foil using the cathodic arc ion plating technique. This was achieved by manipulating the N2 flow rate. The research investigated the impact of N doping on the microstructure, corrosion resistance, interfacial contact resistance (ICR), and hydrophobicity of the a-C films on stainless steel surfaces. The findings reveal that the various a-C films significantly enhance the performance of 304L stainless steel under simulated PEMFCs operating conditions. While N-doped a-C (a-C: N) films are advantageous for reducing ICR, incorporating N results in a decrease in C-sp3 content and density, ultimately leading to a decrease in the corrosion resistance of films. Additionally, the hydrophobicity of the a-C films diminishes with increasing N content. Consequently, N doping is not conducive to improving the overall performance of a-C films on the surface of 304L stainless steel bipolar plates under simulated PEMFCs operating conditions.