Effect of Annealing Temperatures on Recrystallization Behavior and Mechanical Properties of (Fe<sub>50</sub>Mn<sub>30</sub>Co<sub>10</sub>Cr<sub>10</sub>)<sub>97</s ub>Al<sub>3</sub> High-Entropy Alloy

Li Jie,Wu Kaidi,Niu Lichong,Zhang Bo,Zhang Minghe,Feng Yunli
DOI: https://doi.org/10.12442/j.issn.1002-185X.20220911
2023-01-01
Rare Metal Materials and Engineering
Abstract:The (Fe50Mn30Co10Cr10)(97)Al-3 high-entropy alloy (HEA) was designed by adding Al element into the two-phase metastable Fe50Mn30Co10Cr10 HEA. Then, the HEA was treated by rolling and annealing, and the effects of annealing temperature on recrystallization behavior, annealing twin evolution, and the mechanical properties of the alloy were studied. Results show that with increasing the annealing temperature, partial recrystallization, full recrystallization, and grain growth all occur in the alloy. After annealing, HEA exhibits the high recrystallization temperature (0.59T(m)) and high grain coarsening temperature (700 degrees C) due to the severe lattice distortion effect and hysteresis diffusion effect of HEA. A Large number of annealing twins are formed in the alloy annealed at 600 similar to 700 degrees C. With further increasing the annealing temperature (800 similar to 900 degrees C), the content of annealing twins is decreased significantly due to the migration of grain boundaries or twin boundaries. Uniaxial tension results show that the alloy annealed at 700 degrees C has good comprehensive mechanical properties: the tensile strength of 730 MPa and uniform elongation of 50.5%. At the same annealing temperature, the number of annealing twin variants in a single grain is related to the grain size: it is easy to form single annealing twin variant in the small-sized grains and multiple annealing twin variants are easily formed in the large-sized grains.
What problem does this paper attempt to address?