Pt-on-CoNi alloy nanoparticles supported on N and P co-doped graphene catalyst for highly efficient hydrogen evolution by acidic water electrolysis

Fengshun Wu,Li Zeng,An Pei,Yingliang Feng,Lihua Zhu
DOI: https://doi.org/10.1016/j.ijhydene.2024.03.138
IF: 7.2
2024-01-01
International Journal of Hydrogen Energy
Abstract:The multimetallic catalysts with adjustable electronic structures and synergy effect between various metals compared to monometallic catalysts are widely applied in electrocatalysis. Herein, graphene is doped with N and P to prepare rGNP support, then a trimetallic PtCoNi/rGNP catalyst is prepared via simple impregnation and galvanic replacement reaction methods. Pt is highly dispersed on the CoNi alloy nanoparticles (NPs) on rGNP for PtCoNi/rGNP. Based on various characterization techniques and electrochemical testing results such as ICP-OES, XRD, XPS, TEM, HRTEM, STEM, STEM-EDX elemental mapping and line-scanning, it confirms the nanostructure of PtCoNi/rGNP (Pt-on-CoNi alloy). The overpotential of PtCoNi/rGNP for hydrogen evolution (HER) via acidic water electrolysis at 100 mA cm−2 is 15 mV, lower than commercial Pt/C (Pt/C) (66 mV). The Tafel slope of PtCoNi/rGNP is 6.46 mV dec−1, smaller than that of Pt/C (17.15 mV dec−1). The overpotential at 10 mA cm−2 only increases with 3.2 mV (reaching 13.2 mV) after a long time stability testing of 72 h, still lower than Pt/C (20 mV), indicating that it has high catalytic activity and stability. This work not only reveals the synergistic effect mechanism of noble metal-on-non-noble metal for the HER, but also provides a new strategy to develop efficient and highly stable catalysts for the HER.
What problem does this paper attempt to address?