High-performance Fe–6.5wt.%Si/CaCO3 Soft Magnetic Composites Prepared Via the Thermal Decomposition of Calcium Acetate

Hao He,Yang Liu,Zhenghao Cui,Zhenyi Huang,Zhaoyang Wu,Qingyu Hou

DOI: https://doi.org/10.1016/j.jpcs.2024.112012

IF: 4.383

2024-01-01

Journal of Physics and Chemistry of Solids

Abstract:Recent studies on inorganic salt compounds are predominantly directed towards their utilisation as reinforcements for resins. However, the use of salt compounds besides phosphates as insulating layers has not been widely explored. Therefore, this study focuses on using salt compounds as insulating layers for soft magnetic composites (SMCs), revealing their numerous potential advantages. Fe-6.5 wt%Si/(CH 3 COO) 2 Ca composite powders were successfully synthesised using a hydrothermal method. Then, SMCs powders of Fe-6.5 wt%Si/ CaCO 3 and Fe-6.5 wt%Si/CaO, along with their corresponding SMCs, were prepared using powder heat treatment and cold press moulding techniques. The effects of calcium acetate ((CH 3 COO) 2 Ca) addition on the structure and electromagnetic properties of Fe-6.5 wt%Si/CaCO 3 SMCs were further explored via an in-depth investigation of the formation mechanism of CaCO 3 and CaO insulating layers on the surface of the Fe-6.5 wt %Si matrix. Results showed that (CH 3 COO) 2 Ca, as a precursor, decomposed into CaCO 3 at 300 degrees C and CaO at 900 degrees C during heat treatment. Compared with the CaCO 3 insulating layer on the surface of the Fe-6.5 wt%Si matrix, the CaO insulating layer exhibited a tendency for flocculent agglomeration, with lower homogeneity and integrity. Furthermore, the addition of (CH 3 COO) 2 Ca considerably influenced the thickness of the CaCO 3 insulating layer in the Fe-6.5 wt%Si/CaCO 3 SMCs, thereby effectively modulating the magnetic properties of the materials. The prepared Fe-6.5 wt%Si/CaCO 3 SMCs had optimal magnetic properties when 4 wt% (CH 3 COO) 2 Ca was added. Under the conditions of a 25 mT external magnetic field and 100 kHz frequency, the material exhibited a relative magnetic permeability as high as 37.2, a total loss of merely 125.06 kW/m 3 , a saturation magnetic induction intensity of 178.15 emu/g and an electrical resistivity of 125.4 Omega center dot m. The innovative material design and the proposed preparation method considerably enhanced the comprehensive magnetic properties of Fe-6.5 wt%Si-based SMCs, opening up a new avenue for the research and development of high-frequency SMCs.