Distinguishing Bulk Redox from Near-Surface Degradation in Lithium Nickel Oxide Cathodes

Robert Weatherup,Lijin An,Jack Swallow,Peixi Cong,Ruomu Zhang,Andrey Poletayev,Erik Björklund,Pravin Didwal,Michael Fraser,Leanne Jones,Conor Phelan,Namrata Ramesh,Grant Harris,Christoph Sahle,Pilar Ferrer,David Grinter,Peter Bencok,Shusaku Hayama,M. Saiful Islam,Robert House,Peter Nellist,Robert Green,Rebecca Nicholls

DOI: https://doi.org/10.26434/chemrxiv-2024-79nbz

2024-03-20

Abstract:Ni-rich layered cathodes deliver high energy densities, but uncertainties remain about their charge compensation mechanisms and the degradation processes that limit their cycle life. Recent studies have identified trapped molecular O2 within LiNiO2 at high states of charge, as seen for Li-rich cathodes where excess capacity is associated with reversible O2−/O2 redox. Here we show that bulk redox in LiNiO2 occurs by Ni-O rehybridization, lowering the electron density on O sites, but without significant involvement of molecular O2. Trapped O2 is predominantly associated with surface degradation through contact with the electrolyte, and is accompanied by Ni reduction. O2 is removed on discharge, but an excess of Ni2+ remains forming a reduced surface layer that impedes Li transport. Our findings highlight the importance of separating bulk redox from near-surface degradation, and implicate the instability of delithiated LiNiO2 in contact with the electrolyte in surface degradation through O2 formation.

Chemistry

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to distinguish the bulk redox reaction from the near - surface degradation process of lithium nickel oxide (LiNiO2) cathode materials at a high state of charge. Specifically, the research aims to clarify whether the generation of molecular O2 really occurs in LiNiO2 at a high state of charge, especially in the voltage range above 4.3V, and to explore whether this phenomenon is the result of a bulk reaction or surface degradation. In addition, the research also focuses on the impact of these processes on the battery cycle life and how to improve battery performance by understanding these mechanisms.

### Main research contents
1. **Bulk redox reaction**:
- The research found that the bulk redox reaction of LiNiO2 is mainly achieved through Ni - O rehybridization, which reduces the electron density at the oxygen sites, but without significant molecular O2 participation.
- Using X - ray Raman scattering (XRS) technology, the research team observed that at a charging state of 4.8V, the spectra of Ni L3,2 - edge and O K - edge change continuously with the state of charge (SoC), indicating the charge compensation mechanism between Ni and O centers in the bulk.

2. **Near - surface degradation**:
- The generation of near - surface molecular O2 is mainly related to the contact with the electrolyte, accompanied by the reduction of Ni.
- Through fluorescence - yield X - ray absorption spectroscopy (FY - XAS) and total electron - yield (TEY) measurements, the research found that a reduced surface layer (RSL) is formed on the surface, which contains more Ni2+ ions and hinders the transport of Li.
- STEM - EELS analysis further confirmed that the RSL extends about 200 nanometers on the surface, which is related to the penetration of the electrolyte.

### Key conclusions
- **Difference between bulk and surface**: The bulk redox reaction is mainly achieved through Ni - O rehybridization, while the near - surface degradation is mainly related to the generation of molecular O2 and Ni reduction caused by the contact with the electrolyte.
- **Importance of surface degradation**: The RSL formed by surface degradation has a significant impact on battery performance, especially at a high state of charge. Measures need to be taken to stabilize the interface between the cathode material and the electrolyte, rather than just focusing on the bulk stability.

### Significance
- This research emphasizes the importance of distinguishing between the bulk redox reaction and the near - surface degradation, which is of great significance for designing more stable high - energy - density lithium - ion batteries.
- By understanding these mechanisms, more effective strategies can be developed to improve the cycle life and overall performance of the battery.