Abstract:In this study, we mainly focus on the structural morphology and inter-atomic bonding state of tribofilms resulting from a highly-hydrogenated amorphous carbon (a-C:H) film in order to ascertain the underlying mechanisms for its superlubric behavior (i.e., less than 0.01 friction coefficient). Specifically, we achieved superlubricity (i.e., friction coefficients of down to 0.003) with this film in dry nitrogen and argon atmospheres especially when the tribo-pair is made of an a-C:H coated Si disk sliding against an a-C:H coated steel ball, while the a-C:H coated disk against uncoated ball does not provide superlubricity. We also found that the state of superlubricity is more stable in argon than in nitrogen and the formation of a smooth and uniformly-thick carbonaceous tribofilm appears to be one of the key factors for the realization of such superlubricity. Besides, the interfacial morphology of sliding test pairs and the atomic-scale bond structure of the carbon-based tribofilms also play an important role in the observed superlubric behavior of a-C:H films. Using Raman spectroscopy and high resolution transmission electron microscopy, we have compared the structural differences of the tribofilms produced on bare and a-C:H coated steel balls. For the a-C:H coated ball as mating material which provided superlow friction in argon, structural morphology of the tribofilm was similar or comparable to that of the original a-C:H coating; while for the bare steel ball, the sp2-bonded C fraction in the tribofilm increased and a fingerprint-like nanocrystalline structure was detected by high resolution transmission electron microscopy (HRTEM). We also calculated the shear stresses for different tribofilms, and established a relationship between the magnitude of the shear stresses and the extent of sp3-sp2 phase transformation.

The Robust Superlubricity Behaviors of A-C:H Films on Different Roughness Interfaces at Surface Contact Scale

Understanding the interfacial behaviors during superlubricity process of a-C:H film coated on the rough bearing steel surface

Ultra-low Friction of A-C:H Films Enabled by Lubrication of Nanodiamond and Graphene in Ambient Air

The Effect of Roughness Level of A-C:H Films on Its Tribological Behaviors Rubbing Against Steel and Self-Mated Materials

Fullerene-like Nanostructure Induced Excellent Friction Behavior in High Vacuum Environment for Hydrogenated Carbon Film

Origin of Superlubricity in A-C:H:si Films: A Relation to Film Bonding Structure and Environmental Molecular Characteristic

Ion energy-induced nanoclustering structure in a-C:H film for achieving robust superlubricity in vacuum

Evolution of tribo-induced interfacial nanostructures governing superlubricity in a-C:H and a-C:H:Si films

Effect of a-C:H:Si interlayers on the mechanical and superlubricious properties of hydrogenated amorphous carbon films

Enhanced superlubricity on a-C films by lubrication with 3-hydroxypropionic acid

Achieving superlubricity and high adhesion strength of hydrogenated amorphous carbon film with Al/Cr/Si-doping

Influencing mechanisms of deposition bias voltage on superlubricious a-C:H films: Key role of nanoclustering structures in controlling structural evolution of transfer film

Exploring the role of surface hydrogenation in anti-friction of circular-textured amorphous carbon film from the atomic level and its dependence on textured shape

Extreme Contact Pressure-Induced In-Situ Structural Evolution of Nanoclusters Governing Macroscopic Superlubricity in A-C:H Films

Superlow friction and wear enabled by nanodiamond and hexagonal boron nitride on a-C:H films surfaces in dry nitrogen

Low Friction and Wear of a-C:H Films by Lubrication of 3D Graphene/Hexagonal Boron Nitride Composite in Atmospheric Environment

Influence of Tribofilm on Superlubricity of Highly-Hydrogenated Amorphous Carbon Films in Inert Gaseous Environments

Insight into Superlubricity Via Synergistic Effects of Ammonium Tetrathiomolybdate and Hydrogenated Amorphous Carbon Films

Unraveling the friction response from selective hydrogenation of textured amorphous carbon surface

Catalytic superlubricity via in-situ formation of graphene during sliding friction on Au@a-C:H films

3-Hydroxypropionic Acid Triggers Macroscopic Superlubricity on the Diamond-Like Carbon Film