Enhancement of NaYF 4 :Yb 3+ /Er 3+ up-conversion luminescence based on anodized alumina template
Mu Li-Peng,Zhou Yao,Zhao Jian-Xing,Wang Li,Jiang Li,Zhou Jian-Hong,,,
DOI: https://doi.org/10.7498/aps.73.20231405
IF: 0.906
2024-01-01
Acta Physica Sinica
Abstract:Up-conversion nanoparticles (UCNPs) can collect near-infrared (NIR) light and convert it into visible light. Therefore, UCNPs have potential application value in fields such as biomedicine, anti-counterfeiting, and solar cells. However, the conversion efficiency of traditional UCNPs in the above-mentioned fields is relatively low, greatly limiting their application in related fields. Therefore, enhancing the up-conversion luminescence intensity of up-conversion nanoparticles is particularly important and urgently needed. This article utilizes anodic alumina templates to enhance the luminescence intensity of up-conversion nanocrystals. NaYF 4 :Yb 3+ ,Er 3+ with a diameter of 35 nm were prepared using co precipitation method. Single pass AAO templates with pore size and pore spacing of 88 nm and 100 nm were prepared to use two-step anodization method. Finally, NaYF 4 :Yb 3+ ,Er 3+ /AAO composite structures were formed using spin coating method. Compared to NaYF 4 :Yb 3+ ,Er 3+ /Al reference samples, the red green light emission intensity of NaYF 4 :Yb 3+ ,Er 3+ /AAO samples increased by 4.4 and 9.0 times, respectively. The enhancement mechanism was explored using the finite difference time domain method, and the results showed that the primary source of enhancement was the localized surface plasmon resonance effect of the pores in the anodic alumina template. At the same time, the relationship between the up-conversion luminescence intensity of NaYF 4 :Yb 3+ ,Er 3+ /AAO samples and the incident angle was investigated. The experimental results showed that as the incident angle increased, the luminescence intensity of the red and green light of NaYF 4 :Yb 3+ ,Er 3+ /AAO samples first decreased and then increased. Due to the coupling between local surface plasmon resonance and excitation wavelength and emission wavelength, the up-conversion luminescence intensity of the sample can be affected. The relationship between AAO channel enhancement factor and incident angle at excitation wavelength and emission wavelength was studied using the finite difference time domain method. The results indicate that as the incident angle increases, the enhancement factor at the excitation wavelength decreases, while the enhancement factor at the emission wavelength increases after the incident angle of 15°. Therefore, when the incident angle is less than 20°, the electric field intensity at 980 nm dominates, whereas when it is greater than 20°, the electric field intensity at 540 nm and 650 nm takes precedence. The above results provide a reference for applications in the fields of anti-counterfeiting and solar cells.
physics, multidisciplinary