Lead‐Free Relaxor Ferroelectric Ceramics with Ultrahigh Energy Storage Densities via Polymorphic Polar Nanoregions Design
Da Li,Di Zhou,Dong Wang,Weichen Zhao,Yan Guo,Zhongqi Shi,Tao Zhou,Shi‐Kuan Sun,Charanjeet Singh,Sergei Trukhanov,Antonio Sergio Bezerra Sombra
DOI: https://doi.org/10.1002/smll.202206958
IF: 13.3
2022-12-13
Small
Abstract:Polymorphic polar nanoscale design and grain size engineering are proposed to achieve a synergistic improvement in the breakdown strength and the difference between maximum polarization and remnant polarization. An improved recoverable energy density of 8.33 J cm−3 and a high energy efficiency of 90.8% are simultaneously obtained under the electric field of 555 kV cm−1 in Bi0.5Na0.5TiO3‐based relaxor ferroelectric ceramics. One of the long‐standing challenges of current lead‐free energy storage ceramics for capacitors is how to improve their comprehensive energy storage properties effectively, that is, to achieve a synergistic improvement in the breakdown strength (Eb) and the difference between maximum polarization (Pmax) and remnant polarization (Pr), making them comparable to those of lead‐based capacitor materials. Here, a polymorphic polar nanoregions (PNRs) structural design by first introducing 0.06 mol BaTiO3 into Bi0.5Na0.5TiO3 is proposed to construct the morphotropic phase boundary with coexisting structures of micrometer‐size domains and polymorphic nanodomains, enhance the electric field‐induced polarization response (increase Pmax). Then Sr(Al0.5Ta0.5)O3 (SAT)‐doped 0.94 Bi0.5Na0.5TiO3‐0.06BaTiO3 (BNBT) energy storage ceramics with polymorphic PNRs structures are synthesized following the guidance of phase‐field simulation and rational composition design (decrease Pr). Finally, a large recoverable energy density (Wrec) of 8.33 J cm−3 and a high energy efficiency (η) of 90.8% under 555 kV cm−1 are obtained in the 0.85BNBT‐0.15SAT ceramic prepared by repeated rolling process method (enhance Eb), superior to most practical lead‐free competitors increased consideration of the stability of temperature (a variation 5.0 cm−3, η > 90%) at 400 kV cm−1. This strategy provides a new conception for the design of other‐based multifunctional energy storage dielectrics.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology