Abstract:Magnesium hydride (MgH2) offers large capacity for hydrogen storage, but poor thermodynamics and kinetics for releasing hydrogen. In this work, the novel 1D bamboo-shaped carbon nanotubes (BCNTs) are firstly used as carriers for the self-assembly of MgH2 (denoted as MgH2@BCNTs). The high specific surface area (262.3 m(2)g(-1)) and large diameter (over 80 nm) of BCNTs contribute to extremely high loading capacity (76.8 mass fraction), small particle size (15-20 nm) and uniform distribution of MgH2 nanoparticles (NPs). The well-defined MgH2@BCNTs shows remarkably improved thermodynamics and kinetics for H-2 adsorption and desorption. In particular, it starts to release hydrogen at about 220 degrees C, near 170 degrees C lower than that of the commercial MgH2, as well it tends to be hydrogenated even at a relatively low temperature of 100 degrees C by absorbing 3.56 wt% H-2. Moreover, a reversible capacity up to 5.79 wt%, including the "dead weight" of BCNTs, and is well maintained after 10 cycles. The dehydrogenation E-a and Delta H of MgH2@BCNTs can be reduced to 97.97 kJ/mol and 68.92 kJ/mol, which are 111.24 kJ/mol and 6.07 kJ/mol lower than those of the commercial MgH2, respectively. By high pressure densification treatment, the MgH2@BCNTs system achieves an exceptional volumetric capacity up to 65.90 g/L without obvious performance degeneration, resulting from the special structure of BCNTs with inner intervals which works as supports under ultra-high pressure of 750 MPa. Our innovative design of 1D BCNTs supporting MgH2 NPs with high loading weight offers new strategy to synchronously improve the gravimetric and volumetric capacity, as well as the hydrogen storage kinetics and thermodynamics of the nanoconfinement system in the future.

First-principles prediction of Mg decoration on monolayer g-C 6 N 7 as a promising a hydrogen storage media

Enhanced reversible hydrogen storage performance of Mg-decorated g-C 2 N: First principles calculations

Computational exploration of magnesium-decorated carbon nitride (g-C3N4) monolayer as advanced energy storage materials

Mg-decorated CN monolayer with enhanced hydrogen storage

Computational evaluation of Mg-decorated g-CN as clean energy gas storage media

Li decorated graphene like MgN 4 monolayer for hydrogen storage: A first-principles approach

Computational Evaluation of Li-doped g-C2N Monolayer as Advanced Hydrogen Storage Media

Novel 1D Carbon Nanotubes Uniformly Wrapped Nanoscale MgH2 for Efficient Hydrogen Storage Cycling Performances with Extreme High Gravimetric and Volumetric Capacities

First-principles study of Li-doped planar g-C3N5 as reversible H2 storage material

First-principles studies in Mg-based hydrogen storage Materials: A review

Remarkably Improved Hydrogen Storage Properties of Carbon Layers Covered Nanocrystalline Mg with Certain Air Stability

Structures and hydrogen adsorption of (MgCN2)n (n=1–4) clusters

Carbon doping of B 6 N 6 monolayer can improve its hydrogen storage performance effectively: A theoretical study

A DFT study on defects and N doping to enhance hydrogen storage in Mg-decorated graphene

Enhanced Hydrogen Storage Properties of MgH2 by the Synergetic Catalysis of Zr0.4Ti0.6Co Nanosheets and Carbon Nanotubes

Hybrid of Bulk NbC and Layered Nb4C3 MXene for Tailoring Hydrogen Storage Kinetics and Reversibility of Li-Mg-B-H Composite: an Experimental and Theoretical Study

Reversible Hydrogen Storage Media by g-CN Monolayer Decorated with NLi4: A First-Principles Study

Computational exploration of high-capacity hydrogen storage in alkali metal-decorated MgB 2 material

High capacity hydrogen storage structure based on a two-dimensional material (Ga 2 C 6 ) with strong adsorption properties

V 2 N MXene for Hydrogen Storage: First-Principles Calculations

Highly air-stable magnesium hydrides encapsulated by nitrogen-doped graphene nanospheres with favorable hydrogen storage kinetics