Abstract:In this work, thioacetamide (TA) is selected as a sulfur‐containing additive for the precursor solution used in the hydrothermal deposition of Sb2(S,Se)3. With the incorporation of TA, the formation of large voids within the Sb2(S,Se)3 absorber is suppressed, and deep‐level donor‐like defects such as sulfur vacancies are passivated, resulting in enhanced performance of Sb2(S,Se)3 solar cells. Antimony selenosulfide (Sb2(S,Se)3) has recently emerged as a promising light‐absorbing material, attributed to its tunable photovoltaic properties, low toxicity, and robust environmental stability. However, despite these advantages, the current record efficiency for Sb2(S,Se)3 solar cells significantly lags behind their Shockley–Queisser limit, especially when compared to other well‐established chalcogenide‐based thin‐film solar cells, such as CdTe and Cu(In,Ga)Se2. This underperformance primarily arises from the formation of unfavorable defects, predominately located at deep energy levels, which act as recombination centers, thereby limiting the potential for performance enhancement in Sb2(S,Se)3 solar cells. Specifically, deep‐level defects, such as sulfur vacancy (VS), have a lower formation energy, leading to severe non‐radiative recombination and compromising device performance. To address this challenge, thioacetamide (TA), a sulfur‐containing additive is introduced, into the precursor solution for the hydrothermal deposition of Sb2(S,Se)3. This results indicate that the incorporation of TA helps in passivating deep‐level defects such as sulfur vacancies and in suppressing the formation of large voids within the Sb2(S,Se)3 absorber. Consequently, Sb2(S,Se)3 solar cells, with reduced carrier recombination and improved film quality, achieved a power conversion efficiency of 9.04%, with notable improvements in open‐circuit voltage and fill factor. This work provides deeper insights into the passivation of deep‐level donor‐like VS defects through the incorporation of a sulfur‐containing additive, highlighting pathways to enhance the photovoltaic performance of Sb2(S,Se)3 solar cells.

Molecular Induced Patching Process Improving Film Quality for High‐Efficiency Cd‐Free Antimony Selenosulfide Solar Cells

Heterogeneous Nucleation Regulation Amends Unfavorable Crystallization Orientation and Defect Features of Antimony Selenosulfide Film for High‐Efficient Planar Solar Cells

Defect control for high efficiency antimony selenosulfide solar cells by interface Engineering of buried monoatomic aluminum oxide layer

Crystal Growth Promotion and Defect Passivation by Hydrothermal and Selenized Deposition for Substrate-Structured Antimony Selenosulfide Solar Cells

Hydrazine Hydrate‐Induced Surface Modification of CdS Electron Transport Layer Enables 10.30%‐efficient Sb2(S,Se)3 Planar Solar Cells

Solvent‐Assisted Hydrothermal Deposition Approach for Highly‐Efficient Sb2(S,Se)3 Thin‐Film Solar Cells

Optimizing Crystal Orientation and Defect Mitigation in Antimony Selenide Thin-Film Solar Cells through Buffer Layer Energy Band Adjustment

Additive‐Assisted Hydrothermal Growth Enabling Defect Passivation and Void Remedy in Antimony Selenosulfide Solar Cells

Solvent Annealing Enabling Reconstruction of Cadmium Sulfide Film for Improved Heterojunction Quality and Photovoltaic Performance of Antimony Selenosulfide Solar Cells

Pulsed laser deposition of antimony selenosulfide thin film for efficient solar cells

Rapid Thermal‐Driven Crystal Growth and Defect Suppression in Antimony Selenide Thin Film for Efficient Solar Cells

Molecular Beam Epitaxy Deposition of In Situ O‐Doped CdS Films for Highly Efficient Sb2(S,Se)3 Solar Cells

Regulating Deposition Kinetics via A Novel Additive-assisted Chemical Bath Deposition Technology Enables 10.57%-efficient Sb2Se3 Solar Cells

Selenium‐Rich Sb2(S,Se)3 Thin Films Deposited via Sequential Chemical Bath Deposition for High‐Efficiency Solar Cells

Heterojunction Lithiation Engineering and Diffusion-Induced Defects Passivation for Highly Efficient Sb2(S,Se)3 Solar Cells

Defects Passivation via Potassium Iodide Post‐Treatment for Antimony Selenosulfide Solar Cells with Improved Performance

Fabricating High‐Efficiency Sb2(S,Se)3 Solar Cells by Novel Additive‐Assisted Longitudinal Component Engineering

Temperature‐Gradient Solution Deposition Amends Unfavorable Band Structure of Sb2(S,Se)3 Film for Highly Efficient Solar Cells

InCl3-modified SnO2 as Electron Transporting Layer for Cd-free Antimony Selenide solar cells

A Novel Multi-Sulfur Source Collaborative Chemical Bath Deposition Technology Enables 8%-Efficiency Sb2 S3 Planar Solar Cells.

Regulating Energy Band Alignment via Alkaline Metal Fluoride Assisted Solution Post‐Treatment Enabling Sb 2 (S,Se) 3 Solar Cells with 10.7% Efficiency