Optimizing Ternary Blended Sustainable Binder and Water Content in UHPC: Strength, Chloride Resistance and Nanoscale Properties

Peipeng Li,Xinyi Ran,Xin Su,Zhigang Ren

DOI: https://doi.org/10.1016/j.jobe.2024.108722

IF: 7.144

2024-01-01

Journal of Building Engineering

Abstract:This study optimizes the ternary blended sustainable binder and water content in ultra-high performance concrete (UHPC), and explores their underlying effects on strength, chloride resistance and nanoscale properties. The UHPC pastes with cement-ultrafine slag-silica fume blends under various low water-to-binder ratios are developed by utilizing the augmented simplex centroid design method. The compressive strength and resistance to chloride ion penetration of UHPC are investigated and the hydration products and microstructure are characterized by X-ray diffraction (XRD), nitrogen sorption, nanoindentation, and scanning electron microscope (SEM). The results show that ternary blended binder with cement-ultrafine slag-silica is successfully developed for UHPC pastes, achieving a 28-day strength of 141.3 MPa and a chloride ion penetration coefficient of 0.56 x 10-12 m2/s with 30 % ultrafine slag and 5 % silica fume additions. The optimized ternary blended binder system exhibits excellent filling effect and secondary pozzolanic reaction, and promotes more high-density and ultra-high-density C-S-H gels characterized by high modulus and hardness, thus resulting in attenuated intensities of gel and small capillary pores around 3.3 nm and 27 nm, respectively. As the water-to-binder ratio increases from 0.12 to 0.2 in UHPC pastes, the compressive strength experiences a parabolic change, while the chloride resistance suffers from a continuous decrease. The ternary blended binder system in UHPC pastes improves the robustness of chloride resistance under various W/B ratios but makes the compressive strength more sensitive to water content. A lower W/B ratio contributes to lower total porosity but weaker hydration degree and more gel pores around 3 nm, an excessive W/B ratio results in more complete hydration but primarily loose and porous low-density C-S-H gels with lower elastic modulus and hardness. An appropriate W/B around 0.16 is suggested for cement-ultrafine slag-silica fume ternary blended binder in UHPC.