Transport Properties and Specific Heat Ofrusr2gdcu2

X. H. Chen,Zhao-Yan Sun,K. Q. Wang,S. Y. Li,Yimin Xiong,Min Yu,Lei Cao

DOI: https://doi.org/10.1103/physrevb.63.064506

2001-01-01

Abstract:The magnetoresistance (MR) and specific heat in magnetic fields for the samples ${\mathrm{RuSr}}_{2}{\mathrm{GdCu}}_{2}{\mathrm{O}}_{8}$ and ${\mathrm{RuSr}}_{2}{\mathrm{Gd}}_{1.4}{\mathrm{Ce}}_{0.6}{\mathrm{Cu}}_{2}{\mathrm{O}}_{y}$ are presented. Resistive measurements in high magnetic fields show that the field dependence of the transition temperature is significantly different from those observed in other high-${T}_{c}$ cuprates. The sample ${\mathrm{RuSr}}_{2}{\mathrm{GdCu}}_{2}{\mathrm{O}}_{8}$ shows a systematic change in magnetoresistance (MR): The MR is negative at temperatures above the magnetic ordering temperature ${(T}_{\mathrm{Curie}});$ Below ${T}_{\mathrm{Curie}}$ the MR displays a positive peak at low fields, but becomes negative at high fields. However, the sample ${\mathrm{RuSr}}_{2}{\mathrm{Gd}}_{1.4}{\mathrm{Ce}}_{0.6}{\mathrm{Cu}}_{2}{\mathrm{O}}_{y}$ shows a negative MR in the whole measuring temperature range. Both of the samples show a maximum negative magnetoresistance at about ${T}_{\mathrm{Curie}}.$ The specific heat anomaly is suppressed by the field, and the peak-temperature slightly moves down with the field.