Synthesis, Optical Properties, and Applications of Eu3+3+, Na+-doped Plus -Doped High-Color-purity Sr3MgNb2O9 3 MgNb 2 O 9 Red Phosphors for W-Leds and the Detection of Latent Fingerprints
Houteng Zhao,Yilian Ran,Xiya Miao,Siyu Cheng,Dongze Li,Yufeng Du,Xiang Liu,Ruijin Yu
DOI: https://doi.org/10.1016/j.inoche.2024.112922
IF: 3.428
2024-01-01
Inorganic Chemistry Communications
Abstract:A series of novel phosphors, doping Eu3+ 3 + and Na+ + ions in the Sr3MgNb2O9 3 MgNb 2 O 9 (SMNO) crystal lattice (SMNO:xEu3+, x Eu 3 + , x Na + , x = 0.5-30 mol%), was successfully synthesized through high-temperature solid-state reaction. X-ray diffraction (XRD) analysis and Rietveld refinement confirmed the successful synthesis of SMNO:Eu3+, 3 + , Na+. + . The phosphor belongs to the hexagonal crystal system and the P 3 m 1 (No.164) space group. The bandgap energy of SMNO was calculated with Materials Studio and measured with the use of diffuse reflectance spectroscopy. The excitation spectrum of SMNO:Eu3+, 3 + , Na+ + displays multiple narrow absorption peaks in the violet-blue region as well as a charge transfer band (CTB) near 300 nm, exhibiting the highest peak at 394 nm. Four distinct characteristic peaks are observed in the emission spectrum of SMNO:Eu3+, 3 + , Na+. + . Notably, the peak at 601 nm shows the highest emission intensity due to the radiative transition from 5D0 -> 7F2. D 0 -> 7 F 2 . By varying doping concentrations, it was determined that an optimal concentration of 5 mol%Eu3+ 3 + resulted in phosphors, with high color purity exceeding 99 %. Concentration quenching is attributed to the nearest neighbor ions interaction. Furthermore, SMNO:Eu3+, 3 + , Na+ + exhibited good stability in 300-480 K, with luminescent intensity remaining 68.6 % at 420 K and 54.4 % at 480 K compared to room temperature (300 K). The internal quantum efficiency (IQE) of SMNO:5% Eu3+, 3 + , 5 %Na+ + is 65.0 %. Both red and white light-emitting diodes (LEDs) were prepared using SMNO:Eu3+, 3 + , Na+. + . The chromaticity coordinates of w-LED were measured as (0.357, 0.376), correlating to a correlated color temperature (CCT) of 4685 K and exhibiting a good color rendering index (CRI, R a = 88). Additionally, the latent fingerprint (LFP) development demonstrated clear visualization of Levels I-III characteristic structures of fingerprints when utilizing SMNO:Eu3+, 3 + , Na+. + . These findings suggest promising applications for SMNO:Eu3+, 3 + , Na+ + in w-LED lighting and LFP development.