Abstract:Ca-B-Si(CBS) glass doped Ba(Mgl/3Nb2/3)O3(BMN) microwave dielectric ceramics were prepared using the conventional electronic ceramic process.The effects of CBS doping amount on the microwave dielectric properties of BMN ceramics were studied.The results show that an improvement of sintering ability and 1:2 ordering degree of B-site is found in BMN ceramic,which results in the decreasing of microwave dielectric loss.In comparison with pure BMNceramics,the the BMN ceramic doped with 3%(mass fraction) CBS shows a lower sintering temperature decreasing from 1 500 ℃ above to 1 250 ℃,a higher apparent density of 6.32 g/cm3 above,and the best microwave dielectric properties of er = 26,Q.f =67 800 GHz(8 GHz)and τf = 25×10–6/ ℃.That makes it a very promising material to be applied in high frequency microwave device.

Effect of Ca-B-Si Glass Doping on the Microwave Dielectric Properties of Ba(Mg_(l/3)Nb_(2/3))O_3 Ceramics