PIEZOEIECTRIC AND DIELECTRIC PROPERTIES OF PIEZOELECTRIC CERAMICSULPHOALUMINATE CEMENT COMPOSITES

Huang Shifeng,Jun Chang,Futian Liu,XU Rong-hua,Yan Jia-wang,Cheng Xin

2004-01-01

Abstract:Using cement as matrix of piezoelectric smart composites the mismatch problem of smart materials and concrete structure can be solved. The effects of the particle size and mass fraction of 0.08 Pb(Li_(1/4)Nb_(3/4))O_(3)·0.47PbTiO_(3) ·0.45PbZrO_(3) ( on piezoelectric and dielectric properties of the cement matrix composites were studied. The results show that the piezoelectric and dielectric properties of the composites increase rapidly with the increase of particle size of P(ZTNL), but the electromechanical coupling factor K_(p )(planar) and K_(t )(thickness vibration)of the composites decrease. The K_(p )and K_(t)are nearly independent of the size when P(ZTNL) particle size reaches to a certain value. The optimum P(ZTNL) particle size is about 100 μm. With the increasing of P(ZTNL) mass fraction,the piezoelectric and dielectric constants of the composites increase, and the dielectric loss drops down quickly. The composites with better piezoelectric performances can be obtained when the mass fraction of P(ZTNL) content 70%.K_p and K_t of the composite with 85% P(ZTNL) are 28.54% and 28.19% respectively.The dielectric constants of the composites are almost unchanged at -30-100 ℃,which exhibit good dielectrictemperature stability.