Synthesis and Characterization of a Novel Mechanoluminescence Material NaAlSiO<sub>4</sub>:Eu<sup>2+</sup>, Ln<sup>3+</sup>

Haifeng Zhao,Xu‐Sheng Wang,Xiao Feng,Xi Yao

DOI: https://doi.org/10.4028/www.scientific.net/kem.680.220

2016-01-01

Key Engineering Materials

Abstract:Mechanoluminescence (ML) material is a novel functional material, showing a great potential on stress distribution of buildings, machine parts and other solid components. Novel ML materials NaAlSiO 4 :Eu 2+ ,Ln 3+ (Ln=Ho, Nd, Dy) were prepared by a solid-state sintered method, And their microstructure, ML and PL properties were investigated. ML spectra were similar to the PL spectra with an emission band at 550nm, originating from transition 5d-4f of Eu 2+ , and other three emission peaks at 611 nm, 590nm and 578 nm, respectively ascribed to the transitions of 5 D 0 → 7 F 2 , 5 D 0 → 7 F 1 and 5 D 0 → 7 F 0 of Eu 3+ ions. Thermoluminescence (ThL) was measured to characterize traps in NaAlSiO 4 :Eu 2+ ,Ln 3+ (Ln=Ho, Nd, Dy). Diversity of ThL curves demonstrated co-doped Ln 3+ change trap levels in NaAlSiO 4 :Eu 2+ .