Fabrication and Performance Study on Poly(p-Phenylene Terephthamide)porous Membrane

Chu Wang

2014-01-01

Abstract:PPTA porous flat membranes have been fabricated via wet phase-inversion method by using sulphuric acid(H2SO4) as the solvent, polyethylene glycol(PEG) and polyvinylpyrrolidone(PVP) as the pore-creating agents and SiO2 particles as the additive. Membranes′corresponding ultrafiltration performances were characterized by pure water flux, porosity, mechanical strength, and thermostability. The morphologies of PPTA membrane were observed by a field emission scanning electron microscope(FESEM). The results showed that the PPTA porous membrane was a kind of asymmetrical membrane. The increase of SiO2 content, the mixture of pore-creating agents, and the promotion of coagulation bath temperature would bring about an obvious enhancement of the membranes′ permeability. Moreover, the mechanical properties became higher as the rising of SiO2 content, the maximum fracture strength was 1.5 MPa, and the elongation at break increased from 7 % to 14 %. Meanwhlie,there was little effect on thermostability, which made the decomposition temperature of membrane beyond 400 ℃.