Abstract:Albstract The authors synthesized ZnO nanorods by calcining the precursor composed of PVP and Zn(CH3COO)2.2H2O at 300 degrees C. In order to investigate the growth process of ZnO nanorods, the precursor was calcined for different time (0.5, 3, 12, 24 h) and the corresponding products were measured by TEM, HR-TEM (high-resolution transmission electron microscopic), SAED (selected-area electron diffraction pattern) and XRD. The result showed that there were ZnO crystallites in the precursor of PVP and Zn(CH3COO)2.2H2O, which was dried at 110 degrees C. When the precursor was calcined at 300 degrees C for 0.5 h, ZnO nanorods could be observed with diameter of 50 nm and the nanorods consisted of two parts. One was compact nanorod with diameter of about 30 nm and the other part was ZnO crystallites attaching around the nanorod. This phenomenon indicated that there might be a transverse growth direction of ZnO nanorods at early time of crystal growth. When the precursor was calcined for 3 h, the products were direct and smooth single crystal ZnO nanorods. Further increasing the calcining time at 300 degrees C could improve the length of the ZnO nanorods in a certain extent while the diameter changed a little. The HR-TEM results showed that the growth direction of ZnO nanorods was along c axis.

One Step Synthesis of Monodispersed ZnO Nanorods by In-Situ Reaction

Facile synthesis of Zn 1−x Cu x O nanorods with a very broad visible band

Nanostructured ZnO: from Monodisperse Nanoparticles to Nanorods

A Simple and Novel Low-Temperature Hydrothermal Synthesis of ZnO Nanorods

Straight and Thin ZnO Nanorods: Hectogram-Scale Synthesis at Low Temperature and Cathodoluminescence.

Sequential Occurrence of ZnO Nanopaticles, Nanorods, and Nanotips During Hydrothermal Process in a Dilute Aqueous Solution

[The Study on the Growth Process of ZnO Nanorods].

A Novel Low-Temperature Method to Grow Single-Crystal Zno Nanorods

Preparation and characterization of ZnO nanorods

PEG Assisted Hydrothermal Synthesis of ZnO Nanorods

A simple and novel route for the preparation of ZnO nanorods

Synthesis of Single Crystalline CdS Nanorods by a PVP-assisted Solvothermal Method

Controllable Synthesis of Highly Dispersed Zno Nanoparticles and Nanorods

Synthesis and characterization of SnO2 nanorods

Controlled Synthesis of 1D ZnO Nanostructures Via Hydrothermal Process

Influence of Reaction Time on Spherical and Rod-like ZnO Nanocrystals

Synthesis of two kinds of ZnO nanostructures by vapor phase method

Synthesis of Monodispersed Zno Nanorod Array Films by Chemical Solution Deposition.

Synthesis of Branched Zno Nanorods on Various Substrates Via A Wet-Chemistry Route

Formation Mechanism of Nano-ZnO Prepared by Using One-step Method

Hydrothermal Preparation of ZnO Nanorods Using Zinc Powder As Precursor and Their Characterization